TPI Porene® ABS-AN450 Flame Retardant ABS Resin
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Thai Petrochemical Industry Co. LTD. |
| Trade Name | Porene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | TPI Porene® ABS-AN450 Flame Retardant ABS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Melt Flow | 6.5 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.5 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Yield | 42.1 MPa @Thickness 3.17 mm |
6110 psi @Thickness 0.125 in |
|
| Flexural Yield Strength | 63.4 MPa @Thickness 3.17 mm |
9200 psi @Thickness 0.125 in |
|
| Flexural Modulus | 2.14 GPa @Thickness 3.17 mm |
310 ksi @Thickness 0.125 in |
|
| Izod Impact, Notched | 1.28 J/cm @Thickness 6.35 mm |
2.40 ft-lb/in @Thickness 0.250 in |
|
| 1.82 J/cm @Thickness 3.17 mm |
3.41 ft-lb/in @Thickness 0.125 in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 83.0 °C | 181 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | All colors at 1/8 in (3.2 mm) |
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
NC and WT |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 177 °C | 350 °F | |
| Middle Barrel Temperature | 204 °C | 400 °F | |
| Front Barrel Temperature | 216 °C | 420 °F | |
| Melt Temperature | 232 - 249 °C | 450 - 480 °F | Nozzle temp not greater than stock |
| Mold Temperature | 54.4 - 71.1 °C | 130 - 160 °F | |
| Drying Temperature | 87.8 - 93.3 °C | 190 - 200 °F | |
| Dry Time | 2 - 24 hour | 2 - 24 hour | |
| Injection Pressure | 55.2 - 82.7 MPa | 8000 - 12000 psi | |
| Back Pressure | 0.689 MPa | 100 psi | |
| Screw Speed | 50 - 60 rpm | 50 - 60 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Fill Speed | Slow to Moderate |
Users viewing this material also viewed the following:
- Menzolit Menzolit® BMC 0180 Unsaturated Polyester UP
- LG Chemical RS-650 ABS, Extrusion, General Purpose
- Solvay SIPOMER® PAM-4000 Ethylmethacrylate Phosphate; Alkyl Methacrylate Phosphate
- Solvay SOPROPHOR® TS/10-LI Surfactant
- DSM Akulon® F130 PA6
- Eurostar Starpylen HW 30K ECR-BK PP, Injection Molded
- Fainplast Compounds PHA 91 Flexible PVC, Transparent Extrusion
- Adamas Adalon® 118 PTFE, 23/2% Carbon/Graphite Filled
- Amco PRIMATOP HDPE 003955BAS Hexene Copolymer
Copyright © lookpolymers.com All Rights Reserved