LG Chemical TR-558NS Transparent ABS, Antistatic, Natural and Colored Pellets
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical TR-558NS Transparent ABS, Antistatic, Natural and Colored Pellets.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LG transparent ABS has excellent transparency, impact strength, stiffness, and processability. Since its properties are well balanced, it can be applied widely to a variety of electric and electronic parts, OA machines, toys and others that require transparency and high impact strength. An Izod impact strength or falling dart impact strength of LG transparent ABS is relatively similar to that of general ABS, it is not easily cracked like SAN or PMMA resin in the condition of low impact energy. TR-558 series is good for applications requiring high stiffness.Information Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Index of Compound | 22 g/10 min | 22 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength at Break | 51.0 MPa | 7400 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Strength | 77.47 MPa | 11240 psi | ASTM D790 |
| Flexural Modulus | 2.26 GPa | 328 ksi | ASTM D790 |
| Izod Impact, Notched | 0.0981 J/cm | 0.184 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 89.0 °C | 192 °F | Heat deflection temperature, load unknown; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 3.0 % | 3.0 % | |
| Transmission, Visible | 88 % | 88 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 2.00e+13 ohm | 2.00e+13 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 190 - 200 °C | 374 - 392 °F | Extrusion cylinder temperature, C1 |
| 210 - 225 °C | 410 - 437 °F | Extrusion cylinder temperature, C2 | |
| 230 - 240 °C | 446 - 464 °F | Extrusion cylinder temperature, C3 | |
| 240 - 250 °C | 464 - 482 °F | Extrusion cylinder temperature, C4 and C5 | |
| Rear Barrel Temperature | 190 - 200 °C | 374 - 392 °F | |
| Middle Barrel Temperature | 200 - 220 °C | 392 - 428 °F | |
| Front Barrel Temperature | 210 - 230 °C | 410 - 446 °F | |
| Nozzle Temperature | 210 - 230 °C | 410 - 446 °F | |
| Adapter Temperature | 235 - 245 °C | 455 - 473 °F | |
| Die Temperature | 113 - 118 °C | 235 - 245 °F | |
| Melt Temperature | 220 - 240 °C | 428 - 464 °F | Injection molding |
| 255 - 260 °C | 491 - 500 °F | Extrusion | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Roll Temperature | 75.0 - 85.0 °C | 167 - 185 °F | Bottom |
| 80.0 - 90.0 °C | 176 - 194 °F | Middle | |
| 85.0 - 95.0 °C | 185 - 203 °F | Top | |
| Injection Pressure | 68.65 - 88.26 MPa | 9957 - 12800 psi | Second |
| 58.84 - 98.1 MPa | 8534 - 14200 psi | First | |
| Back Pressure | 0.490 - 1.96 MPa | 71.1 - 284 psi | |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm |
Users viewing this material also viewed the following:
- Polimeri Europa Flexirene® MT 40 A Linear Low Density Polyethylene
- SABIC Innovative Plastics EXTEM XH1015 TPI Resin (Asia Pacific)
- SABIC Innovative Plastics Lexan® 923 PC (Asia Pacific)
- SABIC Innovative Plastics Lexan® HF1140 PC (Europe-Africa-Middle East)
- IRPC Polimaxx Pentfoam 241F Expandable Polystyrene
- SABIC Innovative Plastics LNP LUBRICOMP RP003 PA 66
- Sumitomo Bakelite North America RX® 431 Cellulose Reinforced Phenolic Novolac
- Carmel Olefins IPETHENE® 4203 Low Density Polyethylene
- 3M Nextel™ AF-11 w/o sizing Aerospace Woven Fabric 312
- ExxonMobil Iotek® 7310 Zinc Ionomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved