Styron EMERGEâ„¢ 7550 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | EMERGE™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron EMERGEâ„¢ 7550 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
EMERGEâ„¢ PC/ABS 7550 advanced resin is an ignition-resistant PC/ABS blend that contains no chlorine or bromine additives. This resin is suitable for use in a wide variety of applications in the information technology equipment and consumer electronics industries.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 |
| Melt Flow | 10.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
10.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| 46 g/10 min @Load 5.00 kg, Temperature 260 °C |
46 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 46.9 MPa | 6800 psi | ASTM D638 |
| Tensile Strength, Yield | 58.6 MPa | 8500 psi | ASTM D638 |
| Elongation at Break | 80 % | 80 % | ASTM D638 |
| Elongation at Yield | 3.9 % | 3.9 % | ASTM D638 |
| Tensile Modulus | 2.69 GPa | 390 ksi | ASTM D638 |
| Flexural Strength | 95.1 MPa | 13800 psi | ASTM D790 |
| Flexural Modulus | 2.83 GPa | 410 ksi | ASTM D790 |
| Izod Impact, Notched | 5.87 J/cm | 11.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 88.0 °C | 190 °F | IEC 60335-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.6 °C | 195 °F | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.4 °C | 175 °F | unannealed; ASTM D648 |
| Vicat Softening Point | 106 °C | 222 °F | 120°C/hr, 10N; ASTM D1525 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
all colors |
| V-0 @Thickness 2.00 mm |
V-0 @Thickness 0.0787 in |
all colors except natural | |
| Oxygen Index | 28.2 % | 28.2 % | ASTM D2863 |
| Glow Wire Test | 950 °C @Thickness 2.00 mm |
1740 °F @Thickness 0.0787 in |
(GWFI); IEC 60695-2-12 |
| 950 °C @Thickness 2.00 mm |
1740 °F @Thickness 0.0787 in |
(GWIT); IEC 60695-2-13 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 270 °C | 446 - 518 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour |
Users viewing this material also viewed the following:
- MV Labs GD200 GdBr3·xH2O Gadolinium bromide hydrate
- SABIC Innovative Plastics Lexan® EX9332T PC (Europe-Africa-Middle East)
- PolyOne Elastamax™ XL-2185 Thermoplastic Polyolefin Elastomer (TPO (POE))
- IDI Composites 44-10 HGM Thermoset Polyester, Molding
- Lehmann & Voss LUVOCOM® TPE-7711/GY Thermoplastic elastomer, with carbon fiber, electrically conducting
- Schott RG1000 Long Pass Filter
- A. Schulman POLYBATCH™ 7171 POLYBATCH® Concentrate Based In Polyethylene
- Alcoa Toolrite 2011®-T4 Aluminum
- UBE Tyrannohex® Heat Resistant Composite
- Goodfellow Audiolloy® Iron 52/Nickel 48 Alloy
Copyright © lookpolymers.com All Rights Reserved