- Sumitomo Bakelite North America CF 9040A Carbon Fiber Reinforced Phenolic
Sumitomo Bakelite North America CF 9040A Carbon Fiber Reinforced Phenolic
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Carbon Fiber Composite |
| Manufacturer | Sumitomo Bakelite North America |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite North America CF 9040A Carbon Fiber Reinforced Phenolic.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CF 9040A is a high strength carbon fiber phenolic molding compoundInformation provided by Sumitomo Bak North America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.500 g/cc | 0.0181 lb/in³ | ISO 60 |
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Water Absorption | 0.90 % | 0.90 % | ISO 62 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell E | 100 | 100 | ISO 2039/2 |
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527 |
| Flexural Strength | 245 MPa | 35500 psi | ISO 178 |
| Flexural Modulus | 23.0 GPa | 3340 ksi | ISO 178 |
| Compressive Strength | 320 MPa | 46400 psi | ISO 604 |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | ASTM E831 |
| CTE, linear, Transverse to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ASTM E831 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| Form | Pellet | |
| Molding Method | Compression | |
| Injection | ||
| Transfer |
Users viewing this material also viewed the following:
- Parker Chomerics THERM-A-GAP™ GEL 8010 High Performance Fully Cured Dispensable Gel
- LG Chemical 60HR HIPS
- LATI Latamid 6 H2 G/65 PA 6, 65% Glass Fiber Reinforced, Heat Stabilized
- SABIC Innovative Plastics LNP THERMOCOMP AF006XXZ ABS (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ FSU-105-E Concentrate Based In LDPE
- Unitika elitel UE3230 Polyester, Flake
- Toyobo T-772 Nylon, Plating Grade
- ExxonMobil ACHIEVE 3854 Exxpol Metallocene Grade for Nonwovens Fiber and General Extrusion Applications
- BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Dry)
- BP Amoco Accpro® 9117 Enhanced Polypropylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved