- Styron CALIBREâ„¢ 5051 15 Polycarbonate, 5% Glass Reinforced
Styron CALIBREâ„¢ 5051 15 Polycarbonate, 5% Glass Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Styron |
| Trade Name | CALIBRE™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron CALIBREâ„¢ 5051 15 Polycarbonate, 5% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CALIBRE® 5051 is a 5% glass reinforced polycarbonate resin containing mold release for optimal processing. CALIBRE 5051 polycarbonate resin exhibits high modulus and excellent dimensional stability.CALIBRE 5051 polycarbonate resin is typically used for in electrical market applications such as electrical boxes, lighting components and electrical connectors.Available Melt Flow Rate: 15.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM Data |
| Water Absorption | 0.15 % | 0.15 % | |
| Moisture Absorption at Equilibrium | 0.25 % | 0.25 % | Humidity Absorption |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | |
| Melt Flow | 15 g/10 min @Load 1.20 kg, Temperature 300 °C |
15 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM Data |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | |
| Tensile Strength, Ultimate | 48.3 MPa | 7010 psi | ASTM Data |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM Data |
| Elongation at Break | 8.0 % | 8.0 % | ASTM Data |
| Tensile Modulus | 3.10 GPa | 450 ksi | ASTM Data |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM Data |
| Izod Impact, Unnotched | 0.400 J/cm | 0.749 ft-lb/in | ASTM Data |
| Tensile Impact Strength | 147 kJ/m² | 69.9 ft-lb/in² | ASTM Data |
| Impact Test | 46.3 J @Temperature 23.0 °C |
34.1 ft-lb @Temperature 73.4 °F |
Instrumented Dart Total Energy |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 37.8 µm/m-°C @Temperature 20.0 °C |
21.0 µin/in-°F @Temperature 68.0 °F |
ASTM data |
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | Unannealed; ASTM Data |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | Unannealed; ASTM Data |
| Vicat Softening Point | 160 °C | 320 °F | |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
|
| Oxygen Index | 32 % | 32 % |
Users viewing this material also viewed the following:
- Network Polymers NPS 90-0802 Polystyrene
- 3M Dyneon™ Fluorel™ FC-2122 Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR Laminar Filler
- Materion Beryllium Copper Alloy 25 Wire; H (TD04) Temper; 1.3-2.0 mm Diameter (UNS C17200)
- Michelman® Michem® Lube 124 Anionic microcrystalline wax emulsion
- Lehmann & Voss LUVOCOM® 1/CF/20/TF/5 Polyamide 66, with carbon fiber and PTFE, heat stabilized
- Techmer ES Elastoblend® PA6 IM L W
- A. Schulman SCHULAMID® 66 MK40HI 40% Mineral Reinforced, Impact Modified 66
- DuPont Teijin Films Melinex® 359 Polyester Film, 500 Gauge
- Teknor Apex ELEXAR® EL 8732 Thermoplastic Elastomer
Copyright © lookpolymers.com All Rights Reserved