Dow 611A Low Density Polyethylene (LDPE)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE |
| Manufacturer | Dow Chemical |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow 611A Low Density Polyethylene (LDPE).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A shrink film resin with good optics packaging applications Optimum gauge range: 1.0 - 3.0 mil Complies with U.S. FDA 21 CFR 177.1520 (c) 2.1 Information provided by Dow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9239 g/cc | 0.03338 lb/in³ | ASTM D792 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 0.88 g/10 min | 0.88 g/10 min | ASTM D1238 |
| Antiblock Level | 1245 ppm | 1245 ppm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 11.9 MPa | 1730 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.3 MPa | 1780 psi | ASTM D882 |
| Film Elongation at Break, MD | 273 % | 273 % | ASTM D882 |
| Film Elongation at Break, TD | 543 % | 543 % | ASTM D882 |
| Secant Modulus, MD | 0.1970 GPa | 28.57 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.2250 GPa | 32.63 ksi | 2% Secant; ASTM D882 |
| Impact | 666 | 666 | [ft-lbf/in<sup>3</sup>]; Toughness MD; ASTM D882 |
| 770 | 770 | [ft-lbf/in<sup>3</sup>]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 194 g | 194 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 184 g | 184 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 7.64 g/micron | 194 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 7.24 g/micron | 184 g/mil | ASTM D1922 |
| Dart Drop Test | 78.0 g | 0.172 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 25.39 MPa | 3683 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 17.33 MPa | 2513 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 112 °C | 234 °F | Dow Method (DSC) |
| Vicat Softening Point | 97.0 °C | 207 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Gloss | 71 % | 71 % | 45°; ASTM D2457 |
Users viewing this material also viewed the following:
- MV Labs CD200 CdBr2 Cadmium bromide
- MetalTek WASPALOY® Centri-Vac Nickel Cobalt Based Alloy
- LATI Latishield 66-10A H2 CETG/400 PA66, Steel/Glass Fiber Reinforced, Mineral Filled, Heat Stabilized
- Solvay TECHNYLSTARâ„¢ S 216 V35 PA6, 35% glass filled, DRY
- SABIC Innovative Plastics LNP STAT-KON DEF42 PC (Asia Pacific)
- Sumitomo Bakelite North America 2008A Glass Reinforced Hardware Grade Epoxy
- Teknor Apex APEX® 1009 Polyvinyl Chloride, Flexible
- Trelleborg Emerson & Cuming Stycast® 1365-25 Two-Component Epoxy Flexible Encapsulant
- CMT Materials REN Shape® 5169 Foundry Pattern Board
- Arkema Group Oroglas® V 045 I Acrylic, Extrusion Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved