Nilit FRIANYL A63 V2 Nylon 6.6 for injection molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 V2 Nylon 6.6 for injection molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding, flame retardant, free of halogen and phosphorus.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Water Absorption | 2.2 - 3.0 % | 2.2 - 3.0 % | ISO 62 |
| Water Absorption at Saturation | 8.0 - 9.0 % | 8.0 - 9.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.015 - 0.020 cm/cm | 0.015 - 0.020 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 145 MPa | 21000 psi | ISO 2039-1 |
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527 |
| Elongation at Break | 18 % | 18 % | ISO 527 |
| Tensile Modulus | 3.50 GPa | 508 ksi | ISO 527 |
| Flexural Strength | 100 MPa | 14500 psi | ISO 178 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | DIN 53453 |
| NB | NB | ISO 179/1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | DIN 53453 |
| 0.650 J/cm² | 3.09 ft-lb/in² | ISO 179/1eA | |
| 0.550 J/cm² @Temperature -30.0 °C |
2.62 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 125 °C | 257 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 185 °C | 365 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75 |
| Flammability, UL94 | V-2 | V-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | CTI-M 100; IEC 112 |
| 600 V | 600 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- LyondellBasell Petrothene® GA502024 Linear Low Density Polyethylene
- Lehmann & Voss LUVOCOM® 50/TF/15/BK-1 Polycarbonate, with PTFE, easy flowing
- A. Schulman POLYBATCH™ Blue 4500GZ Concentrate Based in Low-Density Polyethylene
- Hexcel® HexForce™ 1527 Fiber Glass Fabric
- Hexcel® HexWeb® HRH-36 - 3/16 - 2.0 Para-Aramid/Phenolic Core
- Dow Corning SYL-OFF® 4000 CATALYST
- 3M Scotch™ 2200 Vinyl Mastic Pads and Rolls
- Arkema Group Appryl® CZT 1030 Polypropylene, 30% Talc/Mica Filled
- REXtac Rextac® RT 4535 Amorphous Polyalphaolefin (APAO)
Copyright © lookpolymers.com All Rights Reserved