Styron CALIBREâ„¢ 201-10 Polycarbonate Resin

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	Styron
Trade Name	CALIBRE™
Port	Shanghai port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Styron CALIBREâ„¢ 201-10 Polycarbonate Resin.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Overview: CALIBREâ„¢ 201-10 is produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. It provides excellent impact resistance, heat distortion resistance and optical clarity. CALIBREâ„¢ 201-10 product is formulated with mold releaseApplications:Food utensilsLiquid containersFood processor housings Packaging applicationsGovt. and Industry Standards:US FDA 21 CFR 177.1580CSAUnderwriters Laboratory (UL)EU food contact 2002/72/ECInformation provided by Styron

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/inÂ³	ISO 1183/A
Linear Mold Shrinkage, Flow	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	ISO 294-4
Melt Flow	10 g/10 min <br>@Load 1.20 kg,<br> Temperature 300 Â°C	10 g/10 min <br>@Load 2.65 lb,<br> Temperature 572 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	71.0 MPa	10300 psi	ISO 527-2/50
Tensile Strength, Yield	60.0 MPa	8700 psi	ISO 527-2/50
Elongation at Break	150 %	150 %	ISO 527-2/50
Elongation at Yield	6.0 %	6.0 %	ISO 527-2/50
Tensile Modulus	2.30 GPa	334 ksi	ISO 527-2/50
Flexural Strength	97.0 MPa	14100 psi	2.0 mm/min; ISO 178
Flexural Modulus	2.40 GPa	348 ksi	2.0 mm/min; ISO 178
Izod Impact, Notched (ISO)	88.0 kJ/mÂ² <br>@Temperature 23.0 Â°C	41.9 ft-lb/inÂ² <br>@Temperature 73.4 Â°F	ISO 180/4A
Izod Impact, Unnotched (ISO)	NB <br>@Temperature 23.0 Â°C	NB <br>@Temperature 73.4 Â°F	ISO 180

Thermal Properties	Metric	English	Comments
Hot Ball Pressure Test	125 Â°C	257 Â°F	IEC 60335-1
Deflection Temperature at 0.46 MPa (66 psi)	144 Â°C	291 Â°F	Annealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi)	125 Â°C	257 Â°F	Unannealed; ISO 75-2/A
	141 Â°C	286 Â°F	Annealed; ISO 75-2/A
Vicat Softening Point	149 Â°C	300 Â°F	ISO 306/B50
Flammability, UL94	HB <br>@Thickness 1.60 mm	HB <br>@Thickness 0.0630 in
	HB <br>@Thickness 3.20 mm	HB <br>@Thickness 0.126 in

Optical Properties	Metric	English	Comments
Transmission, Visible	87 - 97 %	87 - 97 %	ASTM D1003

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	250 V <br>@Thickness 2.00 mm	250 V <br>@Thickness 0.0787 in	IEC 60112