Lanxess DurethanÂ® BKV 115 H2.0 901510 Copolyamide, 15% Glass Fiber

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	Lanxess
Trade Name	Durethan®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lanxess DurethanÂ® BKV 115 H2.0 901510 Copolyamide, 15% Glass Fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

CoPA, injection molding grade, 15% glass fibers, elastomer-modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 15, even in the dry state, good heat-ageing resistance

Physical Properties	Metric	English	Comments
Density	1.23 g/cc	0.0444 lb/inÂ³	ISO 1183
Water Absorption	8.5 %	8.5 %	Test Sim. to ISO 62
Moisture Absorption at Equilibrium	2.5 %	2.5 %	23Â°C/50% R.H.; Test Sim. to ISO 62
Viscosity Test	134 cmÂ³/g	134 cmÂ³/g	Viscosity number; ISO 307, 1157, 1628

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	60.0 MPa	8700 psi	Conditioned; ISO 527-1/-2
	115 MPa	16700 psi	ISO 527-1/-2
Elongation at Break	4.0 %	4.0 %	ISO 527-1/-2
	12 %	12 %	Conditioned; ISO 527-1/-2
Tensile Modulus	2.70 GPa	392 ksi	Conditioned; ISO 527-1/-2
	5.60 GPa	812 ksi	ISO 527-1/-2
Charpy Impact Unnotched	4.00 J/cmÂ² @Temperature -30.0 Â°C	19.0 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/1eU
	4.00 J/cmÂ² @Temperature -30.0 Â°C	19.0 ft-lb/inÂ² @Temperature -22.0 Â°F	Conditioned; ISO 179/1eU
	6.00 J/cmÂ² @Temperature 23.0 Â°C	28.6 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1eU
	7.50 J/cmÂ² @Temperature 23.0 Â°C	35.7 ft-lb/inÂ² @Temperature 73.4 Â°F	Conditioned; ISO 179/1eU
Charpy Impact, Notched	<= 1.00 J/cmÂ² @Temperature -30.0 Â°C	<= 4.76 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/1eA
	<= 1.00 J/cmÂ² @Temperature -30.0 Â°C	<= 4.76 ft-lb/inÂ² @Temperature -22.0 Â°F	Conditioned; ISO 179/1eA
	<= 1.00 J/cmÂ² @Temperature 23.0 Â°C	<= 4.76 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1eA
	1.50 J/cmÂ² @Temperature 23.0 Â°C	7.14 ft-lb/inÂ² @Temperature 73.4 Â°F	Conditioned; ISO 179/1eA
Impact	593	593	Puncture maximum force (N); ISO 6603-2
	542 @Temperature -30.0 Â°C	542 @Temperature -22.0 Â°F	Puncture maximum force (N); ISO 6603-2
Puncture Energy	2.10 J	1.55 ft-lb	ISO 6603-2
	1.70 J @Temperature -30.0 Â°C	1.25 ft-lb @Temperature -22.0 Â°F	ISO 6603-2
	1.70 J @Temperature -30.0 Â°C	1.25 ft-lb @Temperature -22.0 Â°F	Conditioned; ISO 6603-2
Tensile Creep Modulus, 1 hour	2600 MPa	377000 psi	ISO 899-1
Tensile Creep Modulus, 1000 hours	2000 MPa	290000 psi	ISO 899-1

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	30.0 Âµm/m-Â°C	16.7 Âµin/in-Â°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	100 Âµm/m-Â°C	55.6 Âµin/in-Â°F	ISO 11359-1/-2
Melting Point	213 Â°C	415 Â°F	10Â°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	205 Â°C	401 Â°F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	190 Â°C	374 Â°F	ISO 75-1/-2
Deflection Temperature at 8.0 MPa	60.0 Â°C	140 Â°F	ISO 75-1/-2
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in	IEC 60695-11-10
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in	IEC 60695-11-10
Oxygen Index	22 %	22 %	ISO 4589-1/-2

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	300 V	300 V	IEC 60112

Descriptive Properties	Value	Comments
Additives	Release agent
Features	Heat stabilized or stable to heat
	High impact or high impact modified
Form	Pellets
ISO Shortname	ISO 1874-PA 6/66-I, MHR, 14-060, GF15
Processing	Injection molding
Region	Asia Pacific
	Europe
	Near East/Africa
	North America
	South and Central America