- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- Styrolution Terluran® HI-10 ABS
Styrolution Terluran® HI-10 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Styrolution |
| Trade Name | Terluran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Terluran® HI-10 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Terluran HI-10 is an injection molding and extrusion grade of ABS with very high toughness and medium flow.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Water Absorption | 1.03 % | 1.03 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.21 % | 0.21 % | 23°C/50% R.H.; ISO 62 |
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | ASTM Data; MD |
| Melt Flow | 0.10 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.10 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM Test |
| 1.7 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.7 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM Test | |
| 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
8.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 | |
| 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
8.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM Test |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 95 | 95 | ASTM Test |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | 50mm/min; ISO 527 |
| 43.0 MPa | 6240 psi | 2 in/min; ASTM Test | |
| Elongation at Break | 9.0 % | 9.0 % | 50mm/min, Nominal strain; ISO 527 |
| Elongation at Yield | 2.8 % | 2.8 % | 50mm/min; ISO 527 |
| 3.5 % | 3.5 % | 2 in/min; ASTM Test | |
| Tensile Modulus | 1.90 GPa | 276 ksi | 1mm/min; ISO 527 |
| 2.00 GPa | 290 ksi | ASTM Test | |
| Flexural Strength | 56.0 MPa | 8120 psi | ISO Data |
| 66.0 MPa | 9570 psi | ASTM Test | |
| Flexural Modulus | 2.05 GPa | 297 ksi | ASTM Test |
| Izod Impact, Notched | 1.20 J/cm @Temperature -30.0 °C |
2.25 ft-lb/in @Temperature -22.0 °F |
ASTM Test |
| 1.80 J/cm @Temperature -18.0 °C |
3.37 ft-lb/in @Temperature -0.400 °F |
ASTM Test | |
| 4.50 J/cm @Thickness 3.17 mm |
8.43 ft-lb/in @Thickness 0.125 in |
ASTM Test | |
| Izod Impact, Notched (ISO) | 36.0 kJ/m² | 17.1 ft-lb/in² | ISO Test |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| 14.0 J/cm² @Temperature -30.0 °C |
66.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179 |
| 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 95.0 µm/m-°C | 52.8 µin/in-°F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C | 201 °F | ASTM Test |
| 101 °C | 214 °F | ISO 75 | |
| 102 °C | 216 °F | annealed; ASTM Test | |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ASTM Test |
| 96.0 °C | 205 °F | ISO 75 | |
| 98.0 °C | 208 °F | annealed; ASTM Test | |
| Vicat Softening Point | 94.0 °C | 201 °F | Rate "A" Loading 2 (50 degC/h 50N); ASTM Test |
| 94.0 °C | 201 °F | (50 °C/h / 50N) - B/50; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz |
2.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.9 @Frequency 100 Hz |
2.9 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0054 @Frequency 100 Hz |
0.0054 @Frequency 100 Hz |
IEC 60250 |
| 0.0082 @Frequency 1.00e+6 Hz |
0.0082 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 °C | 482 °F | Injection molding |
| Mold Temperature | 102 °C | 216 °F | Ejection temperature |
| Injection Velocity | 60.0 mm/sec | 2.36 in/sec | Injection molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | North America and Europe | |
| FDA | Yes | |
| Form | Pellets | |
| Impact Modified | Yes | |
| NSF Std. 51 | Yes | |
| NSF Std. 61 | No | |
| Primary Processing Technique | Injection Molding | |
| Processing | Injection Molding | |
| Other Extrusion | ||
| Profile Extrusion | ||
| Sheet Extrusion | ||
| UL.UL-C | Yes | |
| USP Class VI | No |
Users viewing this material also viewed the following:
- Polymax® Maxelast® S4730 TPE, PS Overmold
- SABIC Innovative Plastics LNP LUBRICOMP DEL34E PC (Asia Pacific)
- SYNTHOS Koplen® 0513 FR Expandable Polystyrene
- SABIC Innovative Plastics LNP STAT-KON MX01739C PP
- Borealis LE0592 Polyethylene
- A. Schulman POLYPUR™ FPU 1185 Thermoplastic Polyurethane Compound
- Eagle Brass 240 Low Brass, 1/2 Hard
- Ashley Polymers Ashlene® 528L-5G Nylon 66, 5% Glass Reinforced
- Arlon 48271R010 0.010" (0.254 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved