Quadrant EPP Cestilene™ HD 500 R Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded |
| Manufacturer | Quadrant Engineering Plastics Products |
| Trade Name | Cestilene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Quadrant EPP Cestilene™ HD 500 R Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Quadrant Engineering Plastic Products for polymers in their European product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ISO 1183 |
| Water Absorption | 0.010 % | 0.010 % | immersion |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 64 | 64 | after 15 sec.; ISO 868 |
| 66 | 66 | after 3 sec.; ISO 868 | |
| Ball Indentation Hardness | 45.0 MPa | 6530 psi | ISO 2039-1 |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ISO 527 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527 |
| Elongation at Yield | 10 % | 10 % | ISO 527 |
| Tensile Modulus | 1.30 GPa | 189 ksi | ISO 527 |
| Compressive Yield Strength | 9.00 MPa | 1310 psi | at 1% nominal strain; ISO 604 |
| 14.5 MPa | 2100 psi | at 2% nominal strain; ISO 604 | |
| 22.0 MPa | 3190 psi | at 5% nominal strain; ISO 604 | |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 8.50 J/cm² | 40.5 ft-lb/in² | Partial Break; ISO 179/1eA |
| Abrasion | 350 | 350 | Relative loss per DSM internal test (CESTILENE HD 1000 = 100) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 175 - 225 µm/m-°C @Temperature 20.0 °C |
97.2 - 125 µin/in-°F @Temperature 68.0 °F |
|
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | |
| Melting Point | 130 - 135 °C | 266 - 275 °F | ISO 3146; DSC, 10°C/min |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | 20,000 hours continuous |
| 120 °C | 248 °F | for short periods | |
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ISO 75 method A |
| Vicat Softening Point | 80.0 °C | 176 °F | ISO 306 |
| Minimum Service Temperature, Air | -60.0 °C | -76.0 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Oxygen Index | <= 20 % | <= 20 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 93 |
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | IEC 93 |
| Dielectric Constant | 2.4 @Frequency 100 Hz |
2.4 @Frequency 100 Hz |
IEC 250 |
| 2.4 @Frequency 1e+6 Hz |
2.4 @Frequency 1e+6 Hz |
IEC 250 | |
| Dielectric Strength | <= 45.0 kV/mm | <= 1140 kV/in | IEC 243 |
| Dissipation Factor | 0.00020 @Frequency 100 Hz |
0.00020 @Frequency 100 Hz |
IEC 250 |
| 0.00020 @Frequency 1e+6 Hz |
0.00020 @Frequency 1e+6 Hz |
IEC 250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black / green |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 8802 BLK
- Oceanchem Group Antioxidant DLTP
- PPT BP1000 NiZn Ferrite Powder
- Network Polymers NPS 80-0201 Crystal Polystyrene
- NOVA Chemicals EPS M77B Modified Expandable Polystyrene
- SABIC Innovative Plastics LNP KONDUIT ITF2B PA 6/12 (Asia Pacific)
- Overview of materials for Polycarbonate/ASA Alloy, Unreinforced
- Momentive Performance Materials Siloprenâ„¢ LSR 2345/04 Electrically-Conductive Liquid Silicone Rubber
- Haynes 214® alloy, sheet, 1000 hours exposure at 870°C (1600°F)
- LG Chemical Lupoy 1303AH-15 Polycarbonate Resin
Copyright © lookpolymers.com All Rights Reserved