Star Plastics PC1510R Molding Grade PC

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer Star Plastics, Inc
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Star Plastics PC1510R Molding Grade PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Star Plastics, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 16 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 16 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 58.6 MPa
8500 psi
ASTM D638
Tensile Modulus 2.38 GPa
345 ksi
ASTM D638
Flexural Yield Strength 86.2 MPa
12500 psi
ASTM D790
Flexural Modulus 2.38 GPa
345 ksi
ASTM D790
Izod Impact, Notched 6.41 J/cm
12.0 ft-lb/in
73°F, 0.125 in.; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 132 °C
270 °F
unannealed, .125in; ASTM D648
Flammability, UL94 V-2
V-2
.06in
Processing Properties Metric English Comments
Rear Barrel Temperature 271 - 288 °C
520 - 550 °F
Middle Barrel Temperature 277 - 299 °C
530 - 570 °F
Front Barrel Temperature 288 - 316 °C
550 - 600 °F
Nozzle Temperature 288 - 316 °C
550 - 600 °F
Melt Temperature 288 - 316 °C
550 - 600 °F
Mold Temperature 76.7 - 104 °C
170 - 220 °F
Drying Temperature 121 °C
250 °F
Dry Time 4 hour
4 hour
Back Pressure 0.345 - 1.38 MPa
50.0 - 200 psi
Screw Speed 40 - 75 rpm
40 - 75 rpm