Spartech Royalite R59M Hi-Impact ABS/PVC Resin
| Category | Polymer , Thermoplastic , ABS Polymer , ABS/PVC Alloy , Vinyl (PVC) |
| Manufacturer | Spartech |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Spartech Royalite R59M Hi-Impact ABS/PVC Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer. A unique ABS/PVC resin that meets the flammability standards of many industries and is a cost-effective alternative to standard fire-rated ABS. High rigidity in thin sections and consistent, high-quality color and gloss make it ideal for computer housings
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Water Absorption | 0.020 % | 0.020 % | 24 hrs. ASTM D570 |
| Viscosity | 190400 cP @Shear Rate 3000 1/s, Temperature 191 °C |
190400 cP @Shear Rate 3000 1/s, Temperature 375 °F |
Melt Viscosity |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Melt Flow | 1.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 83 | 83 | ASTM D785 |
| Tensile Strength, Yield | 37.6 MPa | 5450 psi | ASTM D638 |
| Modulus of Elasticity | 1.80 GPa | 261 ksi | ASTM D638 |
| Flexural Yield Strength | 57.5 MPa | 8340 psi | ASTM D790 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ASTM D790 |
| Izod Impact, Notched | 7.40 J/cm | 13.9 ft-lb/in | ASTM D256 |
| 1.30 J/cm @Temperature -20.0 °C |
2.44 ft-lb/in @Temperature -4.00 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 155 µm/m-°C @Temperature 20.0 °C |
86.1 µin/in-°F @Temperature 68.0 °F |
ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | Annealed; ASTM D648 |
| Vicat Softening Point | 80.0 °C | 176 °F | ASTM D1525 |
| Flammability, UL94 | 5VA | 5VA | V-0/0.085 in. UL 94 |
| Oxygen Index | 29.9 % | 29.9 % | ASTM D2863 |
Users viewing this material also viewed the following:
- 3M Scotch-Grip™/Fastbond™ 5298 Industrial Adhesive (discontinued **)
- Indium Corp. Indalloy 64 Bismuth Solder Alloy
- Gouda Vuurvast AK 42 Dense Refractory Brick
- SPS Guang Zhou POBUXâ„¢ 3001G10 Flame-retarded/GF10%-PBT
- Techmer ES HiFill® PP 0202 B Polypropylene
- Dow Corning SILASTIC® LS 4-9040 FLUOROSILICONE RUBBER
- Eurotec® Tecotek® PC43 GR20 BK002 PC, 20% glass fiber reinforced, black
- AIM 91Sn/9Zn Solder for Photonic Packaging
- BASF Ultramid® 8202C HS PA6 (Dry)
- Bulk Molding Compounds BMC HT12-1023L Unsaturated Polyester Bulk Molding Compound
Copyright © lookpolymers.com All Rights Reserved