Samyang Triloy® 120H PC/ABS alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Samyang |
| Trade Name | Triloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Triloy® 120H PC/ABS alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics:Impact resistantChemical resistantDimensional stabilityProcessabilityGood flowApplications:Automotive bumperAutomotive outdoor handleAll information provided by Samyang
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.15 % @Time 86400 sec |
0.15 % @Time 24.0 hour |
ASTM D570 |
| Melt Flow | 12 g/10 min @Load 3.80 kg, Temperature 250 °C |
12 g/10 min @Load 8.38 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 53.0 MPa | 7680 psi | ASTM D638 |
| Elongation at Break | 150 % | 150 % | ASTM D638 |
| Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
| Flexural Modulus | 1.72 GPa | 249 ksi | ASTM D790 |
| Izod Impact, Unnotched | 7.35 J/cm @Thickness 3.17 mm |
13.8 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 83.0 µm/m-°C | 46.1 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.00e+16 ohm-cm | 5.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 23.0 kV/mm | 584 kV/in | ASTM D149 |
| Dissipation Factor | 0.0090 @Frequency 1.00e+6 Hz |
0.0090 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 118 sec | 118 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |
| Middle Barrel Temperature | 220 - 240 °C | 428 - 464 °F | |
| Front Barrel Temperature | 210 - 230 °C | 410 - 446 °F | |
| Nozzle Temperature | 240 - 250 °C | 464 - 482 °F | |
| Melt Temperature | 240 - 250 °C | 464 - 482 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Screw Speed | 30 - 80 rpm | 30 - 80 rpm |
Users viewing this material also viewed the following:
- Plenco 50125 PET, Pellet, Injection Molded, White (discontinued **)
- Honeywell Aegis™ HCA155QP Nylon 6/6,6 Extrusion Grade Copolymer (discontinued **)
- IRPC Polimaxx Polene GM2865 High Density Polyethylene
- H.C. Starck Ampersint® MAP FeNi 50/50 For Soft Magnets
- LyondellBasell Hifaxâ„¢ CB272 Thermoplastic Polyolefin Elastomer
- Terio Corporation TZ-1~30 Zirconia
- Braskem GM5240PR HDPE High Density Extrusion Polyethylene
- 3M FP02680N White Polypropylene Label Products
- Aaron Industries AVPS M 100-2 Virgin Polystyrene
- Dow Pellethane® 2354-65D Polyurethane Elastomer, Polyester Polycaprolactone Based (discontinued **)
Copyright © lookpolymers.com All Rights Reserved