SABIC Innovative Plastics GELOY XP7560 ASA (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ASA Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | GELOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics GELOY XP7560 ASA (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GELOY XP7560 is a general purpose ASA/PC injection moulding grade, available in various colours.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.300 % | 0.300 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.80 % | 0.80 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 260 °C |
20 g/10 min @Load 11.0 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 111 | 111 | ISO 2039-2 |
| Hardness, H358/30 | 92.0 MPa | 13300 psi | ISO 2039-1 |
| Tensile Strength at Break | 43.0 MPa | 6240 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 20 % | 20 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 3.7 % | 3.7 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.46 GPa | 357 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 82.0 MPa | 11900 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 95.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
52.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ISO 8302 |
| Hot Ball Pressure Test | <= 95.0 °C | <= 203 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 102 °C | 216 °F | Rate B/50; ISO 306 |
| 107 °C | 225 °F | Rate B/120; ISO 306 | |
| 113 °C | 235 °F | Rate A/50; ISO 306 | |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
UL 94 by SABIC-IP |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- PolyOne Stat-Tech™ ST9620-0020 ES Red Liquid Crystal Polymer + PPS (LCP+PPS)
- Loxim 130 01HB Polycarbonate, 30% Glass Filled, Flame Retardant
- SABIC Innovative Plastics LNP STAT-KON Ultem_UC1200 PEI (Europe-Africa-Middle East)
- Hexcel® HexWeb® HRP/F50 - 4.5 Nonmetallic Flex-Core Honeycomb
- Plenco 4311 Phenolic, Granular, Compression Molded
- Total PPC 11812 S01 Polypropylene, Heterophasic Copolymer, Injection Molding
- Wanhua Chemical Wanthane® WHT-65 TPU Solvent-Based Adhesive
- CLAL-MSX NICLAFOR® 1000 TDX Quenched/Cold Rolled, Drawn Copper Alloy
- Abatron Primkote G A/B Waterborne Epoxy Primer/Sealer for Green Concrete
- A. Schulman ComAlloy Voloy® 462 Glass/Mineral Reinforced, PBT Alloy, Flame Retardant, UL
Copyright © lookpolymers.com All Rights Reserved