Solvay Technyl® C216V15 15% Glass Filled Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® C216V15 15% Glass Filled Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183-A |
| Water Absorption | 1.15 % | 1.15 % | 24 Hr.; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 6.09 GPa | 884 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 5.46 kJ/m² | 2.60 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | ISO 3146-C |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |
| Middle Barrel Temperature | 230 - 240 °C | 446 - 464 °F | Compression Zone |
| Front Barrel Temperature | 240 - 250 °C | 464 - 482 °F | |
| Nozzle Temperature | 241 - 260 °C | 465 - 500 °F | |
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Surface |
| Drying Temperature | 80.0 °C | 176 °F | Dehumidifying Dryer |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Fill Speed | 200 - 600 mm/sec | 7.87 - 23.6 in/sec | Peripheral Screw Speed |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed (cm3/sec) | 120 - 170 cm3/sec |
Users viewing this material also viewed the following:
- MV Labs GE800 GeO2 Germanium(IV) oxide
- PolyOne Geon™ CPVC EC950 Polyvinyl Chloride, Chlorinated (CPVC)
- Nilit FRIANYL B63 HS-GV30 Nylon 6 for injection molding, 30% glass fiber reinforced
- Ineos H20H-00 Polypropylene Homopolymer
- Schott N-KZFS11 Glass
- Williams Advanced Alloys WS280B Solder (Au80/Sn20)
- BASF Elastollan® S95A Polyester Type Polyurethane Elastomer
- Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 35% Cold Reduction + Aged 538°C (1000°F)/4hr/AC