- Solvay Technyl® C 218 V50 50% Glass Filled, Heat Stabilized Nylon 6
Solvay Technyl® C 218 V50 50% Glass Filled, Heat Stabilized Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® C 218 V50 50% Glass Filled, Heat Stabilized Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183-A |
| Water Absorption | 0.75 % | 0.75 % | 24 Hr.; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 225 MPa | 32600 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Tensile Modulus | 14.6 GPa | 2120 ksi | ISO 527 |
| Flexural Strength | 360.00 MPa | 52214 psi | ISO 178 |
| Flexural Modulus | 14.5 GPa | 2100 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 18.9 kJ/m² | 9.00 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | ISO 3146-C |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |
| Middle Barrel Temperature | 230 - 240 °C | 446 - 464 °F | Compression Zone |
| Front Barrel Temperature | 240 - 250 °C | 464 - 482 °F | |
| Nozzle Temperature | 241 - 260 °C | 465 - 500 °F | |
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Surface |
| Drying Temperature | 80.0 °C | 176 °F | Dehumidifying Dryer |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Fill Speed | 200 - 600 mm/sec | 7.87 - 23.6 in/sec | Peripheral Screw Speed |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed (cm3/sec) | 120 - 170 cm3/sec |
Users viewing this material also viewed the following:
- PolyOne LubriOne™ SF-30GF/15T Polyphenylene Sulfide (PPS)
- Styron CALIBREâ„¢ 200 6 Polycarbonate, General Purpose
- ExxonMobil Febis K Series 68
- A. Schulman POLYBATCH™ 60186U Almond Concentrate Based in LLDPE
- DSM Akulon® K222-KGV4 /A PA6-GF20 FR(30)
- Dow Buna® SB 1502 Cold polymerized Emulsion Styrene Butadiene Rubber (E-SBR)
- Dow SPECTRIM™ 50B-S Polyol
- Braskem FPT350WV3 Homopolymer Polypropylene
- Braskem PB208 Injection Molding Low Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved