Overview of materials for Nylon 12, 20% Glass Fiber Filled

Category Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, 20% Glass Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 12, 20% Glass Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.11 - 1.65 g/cc
0.0401 - 0.0596 lb/in³
Average value: 1.21 g/cc Grade Count:22
Filler Content 15.0 - 23.0 %
15.0 - 23.0 %
Average value: 19.5 % Grade Count:4
Water Absorption 0.100 - 1.50 %
0.100 - 1.50 %
Average value: 0.808 % Grade Count:13
Moisture Absorption at Equilibrium 0.500 - 0.800 %
0.500 - 0.800 %
Average value: 0.575 % Grade Count:8
Linear Mold Shrinkage 0.00100 - 0.0120 cm/cm
0.00100 - 0.0120 in/in
Average value: 0.00366 cm/cm Grade Count:16
Linear Mold Shrinkage, Transverse 0.00700 - 0.0120 cm/cm
0.00700 - 0.0120 in/in
Average value: 0.00888 cm/cm Grade Count:8
Melt Flow 3.20 - 12.9 g/10 min
3.20 - 12.9 g/10 min
Average value: 6.37 g/10 min Grade Count:7
Mechanical Properties Metric English Comments
Hardness, Shore D 74.0 - 75.0
74.0 - 75.0
Average value: 74.5 Grade Count:4
Ball Indentation Hardness 95.0 - 115 MPa
13800 - 16700 psi
Average value: 107 MPa Grade Count:3
Tensile Strength, Ultimate 38.0 - 110 MPa
5510 - 16000 psi
Average value: 88.2 MPa Grade Count:25
Elongation at Break 3.00 - 37.0 %
3.00 - 37.0 %
Average value: 7.74 % Grade Count:22
Elongation at Yield 2.70 - 5.00 %
2.70 - 5.00 %
Average value: 3.60 % Grade Count:5
Modulus of Elasticity 2.00 - 9.40 GPa
290 - 1360 ksi
Average value: 5.08 GPa Grade Count:23
Flexural Yield Strength 96.0 - 165 MPa
13900 - 23900 psi
Average value: 128 MPa Grade Count:10
Flexural Modulus 3.45 - 8.00 GPa
500 - 1160 ksi
Average value: 4.59 GPa Grade Count:12
Izod Impact, Notched 0.908 - 1.60 J/cm
1.70 - 3.00 ft-lb/in
Average value: 1.23 J/cm Grade Count:8
Izod Impact, Unnotched 6.14 - 8.01 J/cm
11.5 - 15.0 ft-lb/in
Average value: 7.14 J/cm Grade Count:4
Charpy Impact Unnotched 3.50 - 16.0 J/cm²
16.7 - 76.1 ft-lb/in²
Average value: 7.12 J/cm² Grade Count:17
3.50 - 16.0 J/cm²

@Temperature -30.0 - 30.0 °C
16.7 - 76.1 ft-lb/in²

@Temperature -22.0 - 86.0 °F
Average value: 7.53 J/cm² Grade Count:12
Charpy Impact, Notched 0.600 - 3.00 J/cm²
2.86 - 14.3 ft-lb/in²
Average value: 1.44 J/cm² Grade Count:13
0.600 - 2.00 J/cm²

@Temperature -30.0 - 30.0 °C
2.86 - 9.52 ft-lb/in²

@Temperature -22.0 - 86.0 °F
Average value: 0.996 J/cm² Grade Count:13
Thermal Properties Metric English Comments
CTE, linear 20.0 - 130 µm/m-°C
11.1 - 72.2 µin/in-°F
Average value: 57.4 µm/m-°C Grade Count:11
CTE, linear, Transverse to Flow 80.0 - 150 µm/m-°C
44.4 - 83.3 µin/in-°F
Average value: 133 µm/m-°C Grade Count:6
Melting Point 174 - 185 °C
345 - 365 °F
Average value: 178 °C Grade Count:14
Maximum Service Temperature, Air 90.0 - 150 °C
194 - 302 °F
Average value: 123 °C Grade Count:10
Deflection Temperature at 0.46 MPa (66 psi) 150 - 180 °C
302 - 356 °F
Average value: 169 °C Grade Count:7
Deflection Temperature at 1.8 MPa (264 psi) 55.0 - 165 °C
131 - 329 °F
Average value: 145 °C Grade Count:11
Deflection Temperature at 8.0 MPa 80.0 - 110 °C
176 - 230 °F
Average value: 86.0 °C Grade Count:5
Vicat Softening Point 151 - 175 °C
304 - 347 °F
Average value: 165 °C Grade Count:5
Flammability, UL94 HB - V-2
HB - V-2
Grade Count:13
Electrical Properties Metric English Comments
Electrical Resistivity 10000 - 1.00e+15 ohm-cm
10000 - 1.00e+15 ohm-cm
Average value: 2.14e+14 ohm-cm Grade Count:10
Surface Resistance 1000 - 1.00e+12 ohm
1000 - 1.00e+12 ohm
Average value: 4.65e+11 ohm Grade Count:11
Insulation Resistance 1.00e+9 - 1.00e+12 ohm
1.00e+9 - 1.00e+12 ohm
Average value: 2.78e+11 ohm Grade Count:4
Dielectric Strength 17.5 - 44.0 kV/mm
445 - 1120 kV/in
Average value: 31.6 kV/mm Grade Count:8
Dissipation Factor 0.000335 - 0.0380
0.000335 - 0.0380
Average value: 0.0120 Grade Count:5
Comparative Tracking Index 100 - 600 V
100 - 600 V
Average value: 520 V Grade Count:8
Processing Properties Metric English Comments
Processing Temperature 216 - 266 °C
420 - 510 °F
Average value: 244 °C Grade Count:8
Nozzle Temperature 250 - 260 °C
482 - 500 °F
Average value: 255 °C Grade Count:4
Melt Temperature 190 - 274 °C
374 - 525 °F
Average value: 237 °C Grade Count:6
Mold Temperature 40.0 - 110 °C
104 - 230 °F
Average value: 83.3 °C Grade Count:9
Drying Temperature 75.0 - 110 °C
167 - 230 °F
Average value: 90.8 °C Grade Count:6
Injection Pressure 40.0 - 103 MPa
5800 - 15000 psi
Average value: 77.9 MPa Grade Count:5