Solvay Technyl® A 246M Nylon 66, Impact Grade, EH50
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® A 246M Nylon 66, Impact Grade, EH50.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced and modified polyamide 66, with improved impact resistance, heat stabilized, for injection molding.Technyl A 246m offers an excellent notched impact resistance at low temperatures making it suitable for sports and leisure applications. It is suitable for shoe soles, ski components, ski and surf bindings, as well as toy applications, such as the bumper of a remote-controlled car. This product is available in natural, white and black.Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183-A |
| Water Absorption | 1.05 % | 1.05 % | (Beginning Dry) 24 hours in water 23°C. ISO 62 |
| Linear Mold Shrinkage | 0.019 cm/cm | 0.019 in/in | RHODIA-EP |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in | RHODIA-EP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | ISO 527 |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | ISO 527 |
| Elongation at Break | 210 % | 210 % | ISO 527 |
| Elongation at Yield | 210 % | 210 % | ISO 527 |
| Tensile Modulus | 0.600 GPa | 87.0 ksi | ISO 527 |
| Flexural Yield Strength | 27.0 MPa | 3920 psi | ISO 178 |
| Flexural Modulus | 0.700 GPa | 102 ksi | ISO 178 |
| Izod Impact Resistance | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | NB | NB | ISO 179/EU-1993 |
| Charpy Impact, Notched | 10.0 J/cm² | 47.6 ft-lb/in² | ISO 179/1EA-1993 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | ISO 3146-C |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 93 |
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz |
4.0 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 38.0 kV/mm | 965 kV/in | IEC 243-1 |
| Dissipation Factor | 0.060 @Frequency 1e+6 Hz |
0.060 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 250 - 270 °C | 482 - 518 °F | |
| Middle Barrel Temperature | 260 - 280 °C | 500 - 536 °F | |
| Front Barrel Temperature | 270 - 290 °C | 518 - 554 °F | |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Surface |
| Drying Temperature | 80.0 °C | 176 °F | Dehumidifying Dryer |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Fill Speed | 300 - 600 mm/sec | 11.8 - 23.6 in/sec | Peripheral Screw Speed |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed (cm3/sec) | 80 - 150 cm3/sec |
Users viewing this material also viewed the following:
- Nye Lubricants 868VH (FG) Synthetic Oil
- Plastcom SLOVAMID 66 T 40 Polyamide 66, 40% Mineral Filled
- Arkema Group Kynar Flex® 2950 PVDF Copolymer (discontinued **)
- MarkeTech H-3 Honeycomb Ceramic
- Lubrizol Advanced Materials PEARLBOND® 121 Linear Thermoplastic Polyurethane
- Hardwire 12x-12-12 Medium Density Composite
- Shinkong Synthetic Fibers Shinite® D202G30 PBT, 30% Glass Filled, Fire Retardant
- PlastxWorld CEVIAN® DR210 PC Alloy
Copyright © lookpolymers.com All Rights Reserved