Solvay TECHNYL® C 218L V30 PA6, 30% glass fiber, Eh 0
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® C 218L V30 PA6, 30% glass fiber, Eh 0.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: TECHNYL C 218 L V30 is a polyamide 6 reinforced with 30% glass fiber and UV stabilized.Colors: it is marketed in the natural and black color.Available in: Latin America Main Properties: ? Excellent superficial aspect, Excellent dimensional stability, Good thermal resistance,? UV stabilization and Good impact resistance Applications: TECHNYL C 218 L V30 was developed for applications where good balance of mechanical and thermal properties are required with good superficial aspect.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | 0.95 % @Temperature 23.0 °C, Time 86400 sec |
0.95 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527 |
| Elongation at Break | 3.8 % | 3.8 % | ISO 527 |
| Tensile Modulus | 9.70 GPa | 1410 ksi | ISO 527 |
| Flexural Modulus | 14.3 GPa | 2070 ksi | ISO 178 |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | ISO 75/Af |
| Flammability, UL94 | HB | HB | |
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Glow Wire Test | 650 °C | 1200 °F | ISO 60695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | CEI 93 |
| Dielectric Constant | 3.8 | 3.8 | CEI 250 |
| Dissipation Factor | 0.020 | 0.020 | CEI 250 |
| Comparative Tracking Index | 550 V | 550 V | CEI 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |
| Nozzle Temperature | 240 - 250 °C | 464 - 482 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 230-240°C | |
| Mixing Zone | 240-250°C |
Users viewing this material also viewed the following:
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 30 PHR N550 (FEF) Filler
- Kolon ELLAS K-475A Ester Based Thermoplastic Polyurethane
- Lord Adhesives Fusor® 380NS / 383NS Epoxy Adhesive
- A. Schulman PAPERMATCH® T-4338/50 Specialty Masterbatch
- ExxonMobil 639 Mobil SHC 600 Series
- ExxonMobil Mobil Centaur Moly 2
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, Hardness 64A
- ExxonMobil Mobil Vaculine 146
- Addcomp ADD-VANCE® SA 390 Slip Masterbatch, 30% active ingredients in polypropylene
Copyright © lookpolymers.com All Rights Reserved