Lanxess Durethan® BKV 215 W1 902176 Copolyamide, 15% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 215 W1 902176 Copolyamide, 15% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CoPA, injection molding grade, 15% glass fibers, elastomer-modified, weather-stabilized
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Conditioned; ISO 527-1/-2 |
| 85.0 MPa | 12300 psi | ISO 527-1/-2 | |
| Elongation at Break | 4.9 % | 4.9 % | ISO 527-1/-2 |
| 20 % | 20 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 2.10 GPa | 305 ksi | Conditioned; ISO 527-1/-2 |
| 4.40 GPa | 638 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Impact | 1760 | 1760 | Puncture maximum force (N); ISO 6603-2 |
| 785 @Temperature -30.0 °C |
785 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 7.30 J | 5.38 ft-lb | ISO 6603-2 |
| 3.10 J @Temperature -30.0 °C |
2.29 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 3.10 J @Temperature -30.0 °C |
2.29 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C | 27.8 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 160 µm/m-°C | 88.9 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 214 °C | 417 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 60.0 °C | 140 °F | ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | U.V. stabilized or stable to weather | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6/66-HI,MLR,-050,GF15 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable JJX20A Polyvinyl Chloride, Flexible (PVC, Flexible)
- GRECO ISOTHANE 1055D Poly(adipate)ester TPUÂ Resin
- Techmer ES Plaslube® PC-50/TF/13/SI/2 NAT Polycarbonate
- Samsung Cheil Industries Starex® TX-0510 TRABS, Unreinforced
- Styrolution Terblend® N NM-21 EF Gray 38058 ABS+PA (Dry)
- SABIC Innovative Plastics NORYL NH5020 PPE+PS (Asia Pacific)
- A. Schulman SCHULAMID® 6 GF33RN 33% Glass Bead Reinforced, Industrial Grade Nylon 6
- Chengdu Polyster RPM450 Flame Retardant Masterbatch
- Arlon Thermabond® 99730N004 0.004" (0.102 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
- Beijing Evergrow Resources ER-WR-30G Polypropylene Super-Fine Filter Material
Copyright © lookpolymers.com All Rights Reserved