Solvay TECHNYL® C 216 V40 PA6, 40% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® C 216 V40 PA6, 40% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: TECHNYL® C 216 V40 is a polyamide 6, reinforced with 40% of glass fiber, for injection molding. This product is available in black color.Benefits: The product offers a good combination between thermal and mechanical properties.Available in: Europe and North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: It is used in a wide variety of industries.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183/A |
| Water Absorption | 0.90 % @Temperature 23.0 °C, Time 86400 sec |
0.90 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 215 MPa | 31200 psi | ISO 527 Type 1A |
| Elongation at Break | 2.3 % | 2.3 % | ISO 527 Type 1A |
| Tensile Modulus | 1.31 GPa | 190 ksi | ISO 527 Type 1A |
| Flexural Modulus | 13.0 GPa | 1890 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | 10.7 J/cm² | 50.9 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | ISO 11357 |
| Crystallization Temperature | 190 °C | 374 °F | ISO 11357 |
| Flammability, UL94 | HB @Thickness 0.400 mm |
HB @Thickness 0.0157 in |
1210 |
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
1210 | |
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 | |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
1210 | |
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |
| Front Barrel Temperature | 240 - 250 °C | 464 - 482 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 230-240°C |
Users viewing this material also viewed the following:
- Zircar Zirconia Buster A-30 Alumina Board, Disc, and Cylinder Insulation
- H.C. Starck MoCu 70/30 Molybdenum-Copper Composite Material
- LyondellBasell Astryn BA45H Polypropylene Copolymer, Flame Retardant
- SIDPEC EGYPTENE® HD 5402 EA HDPE Pipe Grade
- SABIC Innovative Plastics LNP THERMOCOMP EC004XXQ PEI
- Lubrizol Estane® ALR E50D Thermoplastic Polyurethane
- CLAL-MSX CUPROROR® TL2 1/2 hard, Copper Alloy
- Dow Corning 3581 Performance Modifier
- Asia International Enterprise (Hong Kong) 60C2 Nylon 66
Copyright © lookpolymers.com All Rights Reserved