Solvay TECHNYL® 52G1MX 25 Grey 7035 PA6, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® 52G1MX 25 Grey 7035 PA6, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Flame retardant polyamide PA6 reinforced with mineral filler for injection molding, also suitable for thin wall parts.Available in: Asia Pacific, Europe, Latin America and North America Product Applications: This phosphorus and halogen free flame retardant grade is particularly suitable for equipment with robust glow wire resistance such as MCB housings. This grade is available in grey color.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | 1.1 % @Temperature 23.0 °C, Time 86400 sec |
1.1 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0075 cm/cm | 0.0075 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0112 cm/cm | 0.0112 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527 Type 1A |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 Type 1A |
| Tensile Modulus | 6.13 GPa | 889 ksi | ISO 527 Type 1A |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | ISO 180/1eU |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ISO 11357 |
| Flammability, UL94 | V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
1210 |
| V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
1210 | |
| V-2 @Thickness 0.800 mm |
V-2 @Thickness 0.0315 in |
1210 | |
| Glow Wire Test | 700 °C @Thickness 0.800 mm |
1290 °F @Thickness 0.0315 in |
ignition temperature; ISO 60695-2-13 |
| 725 °C @Thickness 1.60 mm |
1340 °F @Thickness 0.0630 in |
ignition temperature; ISO 60695-2-13 | |
| 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
ISO 60695-2-12 | |
| 960 °C @Thickness 1.60 mm |
1760 °F @Thickness 0.0630 in |
ISO 60695-2-12 | |
| 960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 220 - 230 °C | 428 - 446 °F | |
| Front Barrel Temperature | 245 - 255 °C | 473 - 491 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 230-240°C |
Users viewing this material also viewed the following:
- Polymer Resources PPX-GP3-[color]-EN Modified-PPO, Extrusion Grade
- Ineos Nova T263B Expandable Polystyrene
- Taiwan Sheen Soon Sheenthane® A8670A Film Grade Thermoplastic Polyurethane Elastomer
- Techmer ES HiFill® PA12 GF30 HS L 30% Glass Filled
- Westlake Plastics Propylux® HS Polypropylene-heat stabilized For Medical Applications
- Barlog Plastics KEBATER BFA15 PBT, 15% glass fiber reinforced, flame retardant
- Polikim KESTAMID® HS Polyamide 6, Heat Resistant
- Beijing Chemical Industry KAIFA® MN-401 PA6 Resin
- Akzo Nobel Trigonox® K-80 Polymerization Initiator
- Arkema Group Nakan® FMS 601 L PVC, Soft Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved