Solvay TECHNYL® 2412GHF6 PA66, 33% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® 2412GHF6 PA66, 33% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamid 66, reinforced with 33% of glass fiber, heat stabilized for injection moldingAvailable in: Asia PacificProduct Applications: TECHNYL® 2412GHF6 is used in all sectors of industry, offering excellent combination between thermal stability and mechanical properties. This grade is widely used for: Hot water distributor pipe, Motor holder for boiler. This product is available in natural and black color and in colors on request.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| Water Absorption | 0.80 % @Temperature 23.0 °C, Time 86400 sec |
0.80 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 200 MPa | 29000 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 300 MPa | 43500 psi | ASTM D790 |
| Flexural Modulus | 9.70 GPa | 1410 ksi | ASTM D790 |
| Izod Impact, Notched | 1.30 J/cm | 2.44 ft-lb/in | ASTM D265 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 4.50 µm/m-°C @Temperature 23.0 - 85.0 °C |
2.50 µin/in-°F @Temperature 73.4 - 185 °F |
ASTM D696 |
| Melting Point | 262 °C | 504 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.800 - 3.20 mm |
HB @Thickness 0.0315 - 0.126 in |
|
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Glow Wire Test | 700 °C @Thickness 1.60 mm |
1290 °F @Thickness 0.0630 in |
IEC-60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 6.00e+13 ohm | 6.00e+13 ohm | IEC 60093 |
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 60243 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 350 V | 350 V | Solution B; IEC 60112 |
| 450 V | 450 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 270 - 275 °C | 518 - 527 °F | |
| Front Barrel Temperature | 285 - 290 °C | 545 - 554 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 275-285°C |
Users viewing this material also viewed the following:
- Precision Polymer Engineering N70M Nitrile Rubber
- Nilit Nilamid A3 H G3 ZB 13% Glass Reinforced High Impact PA66
- Saint-Gobain CHR® SG06-03(R) Premium Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Sinotek Materials WT80-Q Amorphous Graphite Briquettes
- Teknor Apex APEX® 3611-65 Polyvinyl Chloride, Flexible
- Samsung Cheil Industries Starex® EA-0640 ABS, Unreinforced
- SABIC Innovative Plastics Xenoy® XLG2400 PC+PET
- A. Schulman PP 3457-01 Copolymer Polypropylene
- Covestro Makrolon® 2806 Polycarbonate
Copyright © lookpolymers.com All Rights Reserved