Solvay Specialty Polymers Kalix® 2930 HFFR Polyamide, High Performance (HPPA), Glass Fiber

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon
Manufacturer Solvay Specialty Polymers
Trade Name Kalix®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Kalix® 2930 HFFR Polyamide, High Performance (HPPA), Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Kalix® 2930 HFFR is a bio-sourced polyamide-based material specifically formulated to meet UL 94V2 @ 0.4 mm requirements for electronic devices. The material uses an advanced halogen-free flame retardant package expressly designed to minimize blooming, plate out, and other process related issues commonly associated with flame retardant materials.Features: Fast Molding Cycle; Flame Retardant; Good Dimensional Stability; Good Impact Resistance; Good Surface Finish; High Flow; High Stiffness; High Strength; Hot Water Moldability; Low Warpage; Paintable; PlatableUses: Cell Phones; Electrical Parts; Electrical/Electronic Applications; Thin-walled PartsInjection Molding Notes: Kalix® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Kalix® resins be dried prior to molding.Additional Properties: Flexural Strain at Break - ISO 178 2.6 %; Specific Gravity - 1.41; UL RatingInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Water Absorption 0.17 %

@Time 86400 sec
0.17 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Stress 130 MPa
18900 psi
ISO 527-2
Elongation at Break 2.4 %
2.4 %
ISO 527-2
Tensile Modulus 10.6 GPa
1540 ksi
ISO 527-2
Flexural Strength 200 MPa
29000 psi
ISO 178
Flexural Modulus 10.0 GPa
1450 ksi
ISO 178
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
Type 1, Notch A; ISO 180
Izod Impact, Unnotched (ISO) 55.0 kJ/m²
26.2 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Melting Point 223 °C
433 °F
DSC
Glass Transition Temp, Tg 65.0 °C
149 °F
DSC
Processing Properties Metric English Comments
Rear Barrel Temperature 265 - 275 °C
509 - 527 °F
Front Barrel Temperature 280 - 295 °C
536 - 563 °F
Melt Temperature 260 - 300 °C
500 - 572 °F
Mold Temperature 80.0 - 120 °C
176 - 248 °F
Drying Temperature 80.0 °C

@Time 14400 - 43200 sec
176 °F

@Time 4.00 - 12.0 hour
Moisture Content <= 0.090 %
<= 0.090 %
Descriptive Properties Value Comments
Availability Asia Pacific; North America
Color Black
Form Pellets
Part Marking Code >PA610-GF30<
ISO 11469
Processing Technique Injection Molding; Water-Heated Mold Injection Molding