PolyOne Novablend™ 9562 Polyvinyl Chloride Alloy (PVC Alloy)
| Category | Polymer , Thermoplastic , Vinyl (PVC) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Novablend™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Novablend™ 9562 Polyvinyl Chloride Alloy (PVC Alloy).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Custom MoldingInformation provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | Properties reported for Natural color.; ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Spiral Flow | 58.4 cm | 23.0 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 79 | 79 | 10 sec; ASTM D2240 |
| Tensile Strength, Yield | 46.2 MPa | 6700 psi | Type I, 51 mm/min; ASTM D638 |
| Elongation at Break | 50 % | 50 % | Type I, 51 mm/min; ASTM D638 |
| Tensile Modulus | 2.24 GPa | 325 ksi | Type I, 51 mm/min; ASTM D638 |
| Flexural Strength | 68.3 MPa | 9910 psi | ASTM D790 |
| Flexural Modulus | 2.28 GPa | 331 ksi | ASTM D790 |
| Izod Impact, Notched | 1.30 J/cm @Thickness 3.18 mm, Temperature -18.0 °C |
2.44 ft-lb/in @Thickness 0.125 in, Temperature -0.400 °F |
Injection Molded; ASTM D256A |
| 6.40 J/cm @Thickness 3.18 mm, Temperature 0.000 °C |
12.0 ft-lb/in @Thickness 0.125 in, Temperature 32.0 °F |
Injection Molded; ASTM D256A | |
| 9.60 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
18.0 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A | |
| Dart Drop Total Energy | 89.0 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.167 ft-lb/mil @Thickness 0.125 in, Temperature 73.4 °F |
Procedure A, 1/8-in. conical No brittle breaks. MFE/Avg. thk. > 264/0.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 140 µm/m-°C | 77.8 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 77.3 °C @Thickness 3.18 mm |
171 °F @Thickness 0.125 in |
Injection Molded; Unannealed; ASTM D648 |
| 82.0 °C @Thickness 3.18 mm |
180 °F @Thickness 0.125 in |
Injection Molded; Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.4 °C @Thickness 3.18 mm |
148 °F @Thickness 0.125 in |
Injection Molded; Unannealed; ASTM D648 |
| 74.1 °C @Thickness 3.18 mm |
165 °F @Thickness 0.125 in |
Injection Molded; Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 199 - 210 °C | 390 - 410 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Opaque | |
| Features | General Purpose | |
| High Impact Resistance | ||
| Medium Flow | ||
| Forms | Pellets | |
| Generic Material | PVC Alloy | |
| Generic Name | Polyvinyl Chloride Alloy (PVC Alloy) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Construction Applications | |
| General Purpose | ||
| Outdoor Applications |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP KONDUIT PX10322 PA 6 (Asia Pacific)
- Nilit Nilamid B3 H G10 50% Glass Fiber Reinforced PA6
- SABIC Innovative Plastics LNP LUBRICOMP ZP001XXP PPE+PS
- Solvay RHODACAL® A-246/L Surfactant
- Eurostar Starflam PX06010 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
- Eurotec® Tecomid® NA40 GR14 NL MC PA6.6, 14% glass fiber reinforced, impact modified, heat stabilized, natural
- Overview of materials for Polystyrene + Polyphenylene Ether, Glass Filler