Solvay Specialty Polymers Ixef® 1022 Polyarylamide (PARA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyarylamide (PAA) , Polyarylamide, Glass Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® 1022 Polyarylamide (PARA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ixef 1022 is a 50% glass-fiber reinforced, general purpose polyarylamide compound which exhibits very high strength and rigidity, outstanding surface gloss, and excellent creep resistance. Ixef 1022/0006 (natural) and Ixef 1022/9006 (black) are in compliance with ISO 10993 for limited exposure (less than 24 hours) medical applications. Ixef resin is well-suited for applications involving contact with cold water. Ixef 1022 is approved for food contact meeting European standard 10/2011/EC for both black (Ixef 1022/9006) and natural (Ixef 1022/0006). Ixef 1022 also meets the following European water approval standards: French positive list (FPL): Ixef 1022/0006 (natural) and Ixef 1022/0008 (natural); KTW (cold water only): Ixef 1022/0006 (natural) and Ixef 1022/9006 (black); ACS: Ixef 1022/9006 (black). - Black: 1022/9006 (ISO 10993 compliant) and Ixef 1022/9008 - Natural: 1022/0006 (ISO 10993 compliant) and Ixef 1022/0008 - Other Colors Available - Custom ColorableInjection Notes: Hot runners: 250°C to 260°C (482°C to 500°F) Drying The material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F). Injection Molding IXEF 1022 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The measured melt temperature should be about 280°C (536°F), and the barrel temperatures should be around 250 to 260°C (482 to 500°F) in the rear zone, gradually increasing to 260 to 290°C (500 to 554°F) in the front zone. If hot runners are used, they should be set to 250 to 260°C (482 to 500°F). To maximize crystallinity, the temperature of the mold cavity surface must be held between 120 and 140°C (248 and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95-99%).Data is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.64 g/cc
0.0592 lb/in³
ISO 1183
Filler Content 50 %
50 %
Glass Fiber Reinforcement
Water Absorption 0.16 %

@Temperature 23.0 °C,
Time 86400 sec
0.16 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 1.5 %
1.5 %
65% RH; Internal Method
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 260 MPa
37700 psi
Conditioned; ISO 527-2
280 MPa
40600 psi
ISO 527-2
Elongation at Break 1.9 %
1.9 %
ISO 527-2
2.2 %
2.2 %
Conditioned; ISO 527-2
Tensile Modulus 20.0 GPa
2900 ksi
Conditioned; ISO 527-2
20.0 GPa
2900 ksi
ISO 527-2
Flexural Strength 400 MPa
58000 psi
ISO 178
Flexural Modulus 19.0 GPa
2760 ksi
ISO 178
Izod Impact, Notched 1.10 J/cm
2.06 ft-lb/in
ASTM D256
8.50 J/cm
15.9 ft-lb/in
ASTM D256
Charpy Impact Unnotched 7.00 J/cm²
33.3 ft-lb/in²
ISO 179
Charpy Impact, Notched 1.10 J/cm²
5.23 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 15.0 µm/m-°C
8.33 µin/in-°F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 230 °C
446 °F
Unannealed; ISO 75-2/A
UL RTI, Electrical 130 °C

@Thickness 1.50 mm
266 °F

@Thickness 0.0591 in
UL 746
UL RTI, Mechanical with Impact 90.0 °C

@Thickness 0.750 mm
194 °F

@Thickness 0.0295 in
UL 746
105 °C

@Thickness 1.50 mm
221 °F

@Thickness 0.0591 in
UL 746
UL RTI, Mechanical without Impact 105 °C

@Thickness 0.750 mm
221 °F

@Thickness 0.0295 in
UL 746
120 °C

@Thickness 3.00 mm
248 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 HB
HB
UL 94
Oxygen Index 25 %
25 %
ISO 4589-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 4.6

@Frequency 110 Hz
4.6

@Frequency 110 Hz
IEC 60250
Dielectric Strength 31.0 kV/mm
787 kV/in
IEC 60243-1
Dissipation Factor 0.017

@Frequency 110 Hz
0.017

@Frequency 110 Hz
IEC 60250
Comparative Tracking Index 570 V
570 V
IEC 60112
400 - 600 V

@Thickness 3.00 mm
400 - 600 V

@Thickness 0.118 in
PLC 1; UL 746
Hot Wire Ignition, HWI >= 120 sec

@Thickness 1.50 mm
>= 120 sec

@Thickness 0.0591 in
PLC 0; UL 746
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 1.50 mm
>= 120 arcs

@Thickness 0.0591 in
PLC 0; UL 746
High Voltage Arc-Tracking Rate, HVTR 0.000 - 10.0 mm/min

@Thickness 3.00 mm
0.000 - 0.394 in/min

@Thickness 0.118 in
PLC 0; UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Nozzle Temperature 260 - 290 °C
500 - 554 °F
Melt Temperature 280 °C
536 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Drying Temperature 120 °C
248 °F
Dry Time 0.500 - 1.50 hour
0.500 - 1.50 hour
Descriptive Properties Value Comments
Agency Ratings ACS Unspecified Rating
Black only
EU No 10/2011
ISO 10993
ISO 10993-Part 1
KTW Unspecified Rating
Cold Water Only
Appearance Black
Colors Available
Natural Color
Automotive Specifications ASTM D6779 PA111G50
BOSCH N28 BN05-OX1 BN0508-GF50-3Anf08SO Color: 0008 Natural
BOSCH N28 BN05-OX1 BN0508-GF50-3Asw01SO Color: 9008 Black
GM GM7001M PAMXD6(A4,A22,A64,BA651,G30,MS1700,NS335) Color: 9008 Black
GM GM7001M PAMXD6(A4,A22,A64,BA751,G30,MS1700,NS350) Color: NT Natural
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Biocompatible
E-beam Sterilizable
Ethylene Oxide Sterilizable
General Purpose
Good Chemical Resistance
Good Creep Resistance
Good Dimensional Stability
Good Sterilizability
High Flow
High Strength
Low Moisture Absorption
Outstanding Surface Finish
Radiation (Gamma) Resistant
Radiation Sterilizable
Radiotranslucent
Ultra High Stiffness
Forms Pellets
Generic PARA
Injection Rate Fast
Processing Method Injection Molding
RoHS Compliance RoHS Compliant
Uses Appliances
Automotive Applications
Automotive Interior Parts
Cell Phones
Dental Applications
Food Service Applications
Furniture
High Gloss Applications
Hospital Goods
Medical Appliances
Medical/Healthcare Applications
Sporting Goods
Surgical Instruments