Schwartz Technical Plastics LAMIGAMID® 300 Cast Polyamide 6, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Cast |
| Manufacturer | Schwartz Technical Plastics |
| Trade Name | LAMIGAMID® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schwartz Technical Plastics LAMIGAMID® 300 Cast Polyamide 6, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Application: slippers and center blocks for heavy rolling mills, outrigger floatsInformation provided by Schwartz Technical Plastics GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO R 1183 |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | DIN 53473 |
| Water Absorption at Saturation | <= 7.0 % @Temperature 20.0 °C |
<= 7.0 % @Temperature 68.0 °F |
ISO R 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 130 MPa | 18900 psi | Hc 30; ISO 2039; partially |
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | ISO-DIS 527 |
| Creep Strength | >= 15.0 MPa | >= 2180 psi | 1% elongation, 1000 h; DIN 53444 |
| >= 20.0 MPa | >= 2900 psi | 2% elongation, 1000 h; DIN 53444 | |
| Tensile Modulus | 3.20 GPa | 464 ksi | DIN 53457 |
| Flexural Strength | 110 MPa | 16000 psi | DIN 54352 |
| Flexural Modulus | 2.70 GPa | 392 ksi | DIN 53457 |
| Compressive Strength | 29.0 MPa | 4210 psi | 5% pressing; EN ISO 604 |
| 45.0 MPa | 6530 psi | 10% pressing; EN ISO 604 | |
| 65.0 MPa | 9430 psi | 20% pressing; EN ISO 604 | |
| Izod Impact, Notched (ISO) | >= 8.00 kJ/m² | >= 3.81 ft-lb/in² | ISO 180-1A |
| Izod Impact Resistance | NB | NB | swinging hammer 0,1 DIN 51222; DIN 53453 |
| Coefficient of Friction | 0.040 | 0.040 | With lubrication |
| Coefficient of Friction, Dynamic | 0.35 | 0.35 | no lube; Steel 2162, Rvst=2E-6m, p=0.05 Mpa, v=0.6 m/s, t=40°C |
| Tear Strength Test | >= 0.30 | >= 0.30 | ISO-DIS 527 |
| K Factor (Wear Factor) | 8.0e-11 | 8.0e-11 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 - 80.0 µm/m-°C @Temperature 20.0 - 100 °C |
38.9 - 44.4 µin/in-°F @Temperature 68.0 - 212 °F |
DIN 53752 |
| Specific Heat Capacity | 1.67 J/g-°C | 0.399 BTU/lb-°F | |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 200 - 220 °C | 392 - 428 °F | ISO R 1218 |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous |
| 180 °C | 356 °F | Intermittent | |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | V-notch; ISO R 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | V-notch; ISO R 75 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | Continuous |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | DIN 53482 |
| Dielectric Constant | 3.7 | 3.7 | DIN 53483 |
| Dielectric Strength | 50.0 kV/mm | 1270 kV/in | DIN 53481 |
| Dielectric Loss Index | 0.030 | 0.030 | DIN 53483 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Creepage/leakage Resistance | KA3c | DIN 53480 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3970H TPE, PP Overmold or Standalone use
- Process Technologies Inc Silicone-White Sanitary Gasket
- Polymer Resources PC-GP3-TFE10 Polycarbonate, 10% PTFE, High Flow, Wear Resistant
- Meehanite CR Corrosion Resisting Cast Iron
- Michelman® Michem® Lube 190 Anionic polyethylene wax emulsion
- Solvay Specialty Polymers KetaSpire® KT-880 NL Polyetheretherketone (PEEK)
- Trelleborg B568 High Quality Nitrile Rubber
- Eagle Brass 706 Copper Nickel 10%, Annealed
- ChevronTexaco Mechanism LPS® ISO 15 Hydraulic Oil
- Advanced Polymer Alloys Alcryn® 2160 NC Melt Processable Rubber
Copyright © lookpolymers.com All Rights Reserved