- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- Sax Polymers SAXLAC 310T Acrylonitrile Butadiene Styrene
Sax Polymers SAXLAC 310T Acrylonitrile Butadiene Styrene
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Sax Polymers |
| Trade Name | SAXLAC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXLAC 310T Acrylonitrile Butadiene Styrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Saxalac 310T is an antistatic, high impact resistant ABS injection molding grade, characterized by good processability and high stiffness.Mechanical property data tested at 50% RH.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Melt Flow | 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
7.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
from MVR; ISO 1033 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 40.0 MPa | 5800 psi | ISO 527-1 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1 |
| Tensile Modulus | 1.90 GPa | 276 ksi | ISO 527-1 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 30.0 kJ/m² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 100 kJ/m² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180 |
| 100 kJ/m² @Temperature -30.0 °C |
47.6 ft-lb/in² @Temperature -22.0 °F |
ISO 180 | |
| Charpy Impact Unnotched | 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| 10.0 J/cm² @Temperature -30.0 °C |
47.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 2.80 J/cm² @Temperature 23.0 °C |
13.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 95.0 °C @Thickness 2.00 mm |
203 °F @Thickness 0.0787 in |
IE/CEN 60335-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 96.0 °C | 205 °F | 50B; ISO 306 |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IE/CEN 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- Nabaltec SYMULOX® Z 72 Synthetic Sintered Mullite
- PolyOne Geon™ 170 Series L120UF Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- LNP Lubricomp® LCL-4033 EM Polyetheretherketone, Carbon Fiber Reinforcement, PTFE Lubricant (discontinued **)
- Sibur Nitrilast-26M Nitrile-Butadiene Rubber (NBR)
- Total 5502 HDPE, blow molding, pipe
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 60 PHR Non-Black, Aerosil 200
- ChevronTexaco HiPerSYN™ ISO 46 Oil
- A. Schulman ComAlloy Comtuf® 611 Nylon 6, Glass Reinforced, Impact Modified
- BASF Dimethyldicykan 3,3’-Dimethyl-4,4’-diamino-dicyclohexylmethane
Copyright © lookpolymers.com All Rights Reserved