Hexcel® F161 Epoxy Resin, 120 Glass Fabric
| Category | Polymer , Thermoset , Epoxy , Epoxy/Glass SMC |
| Manufacturer | Hexcel |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® F161 Epoxy Resin, 120 Glass Fabric.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Hexcel designation: 120-38"-F161; Fiber: 450-1/2Information provided by HexCel
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 400 MPa @Temperature 177 °C |
58000 psi @Temperature 351 °F |
|
| 455 MPa @Temperature 24.0 °C |
66000 psi @Temperature 75.2 °F |
||
| Tensile Modulus | 18.0 GPa @Temperature 177 °C |
2610 ksi @Temperature 351 °F |
|
| 21.0 GPa @Temperature 24.0 °C |
3050 ksi @Temperature 75.2 °F |
||
| Compressive Yield Strength | 296 MPa @Temperature 177 °C |
42900 psi @Temperature 351 °F |
|
| 482 MPa @Temperature 24.0 °C |
69900 psi @Temperature 75.2 °F |
||
| Compressive Modulus | 20.0 GPa @Temperature 177 °C |
2900 ksi @Temperature 351 °F |
|
| 21.0 GPa @Temperature 24.0 °C |
3050 ksi @Temperature 75.2 °F |
Users viewing this material also viewed the following:
- Styron CALIBREâ„¢ 7101 15 Polycarbonate, 10% Glass Reinforced
- A. Schulman FORMION™ FI 301 Ionomer
- Borealis Visico™/Visico™ LE4421M/LE4431M Polyethylene
- A. Schulman SCHULAMID® 66 MK4015H 40% Glass Fiber/Mineral Reinforced, Heat Stabilized Nylon 66
- A. Schulman POLYFLAM™ FPP 1007 Talc Filled Homopolymer Polypropylene
- ConocoPhillips IGL-9 Enclosed Gear Lubricant ISO 1000, AGMA Number 8A EP
- 3A Composites Core Materials AIREX® C70.250 Universal Structural Foam
- Azdel SuperLite® SL551200-100 PP Resin Matrix / 55% Glass Fiber (7 mm Molded Thickness)
- Total Xsene® XS10 YS HDPE, pipe
Copyright © lookpolymers.com All Rights Reserved