- HOME
- POLYMER SEARCH
- Thermoplastic
- Nylon
- Nylon 66
- Nylon 66, 20% Glass Fiber Filled
- Sax Polymers SAXAMID 236F4Q32 Nylon 6.6, 20% Glass Fiber
Sax Polymers SAXAMID 236F4Q32 Nylon 6.6, 20% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled , Nylon 66, Glass Reinforced, Impact Grade |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 236F4Q32 Nylon 6.6, 20% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 236 F4Q32 is a impact-modified polyamide 6.6 injection-molding-grade reinforced with 20% glass fibers and very good flow properties. It is suitable for applications requiring toughness in combination with low creep properties.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 115 MPa | 16700 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 3.4 % | 3.4 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 5.50 GPa | 798 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 163 MPa | 23600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.80 GPa | 696 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 90.0 kJ/m² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 6.90 J/cm² @Temperature -30.0 °C |
32.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.70 J/cm² @Temperature 23.0 °C |
8.09 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 235 °C | 455 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- MV Labs ER870 Er2(C2O4)3·xH2O Erbium oxalate hydrate
- PolyOne OnFlex™ S FR 60A-3S1846 Thermoplastic Elastomer (TPE)
- DuPont™ Clysar® VHP Polyolefin Shrink Packaging Film, 50 Gauge (discontinued **)
- Lord Adhesives 9010 Medium Viscosity, Odorless, Non-Frosting Methoxyethyl Cyanoacrylate Adhesive
- Solvay TECHNYLSTARâ„¢ SX 218 L2 V60 Black JA6A PA6, 60% glass filled, Conditioned
- Techmer ES Electrablend® PC/ABS
- Dow UNIVAL™ DMDA-6320 NT 7 High Density Polyethylene Resin (HDPE)
- Barlog Plastics KEBAFLOW MX130 LCP, 30% glass fiber / mineral reinforced
- Multibase Multibatch® MP 53857 Sheet Extrusion
- NOVA Chemicals Novapol® HB-L455-A HDPE Blow Molding Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved