- Sax Polymers SAXAMID 126F2K4 Nylon 6, Glass Fiber/Bead Filled
Sax Polymers SAXAMID 126F2K4 Nylon 6, Glass Fiber/Bead Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled , Nylon 6, Glass Bead Filled |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 126F2K4 Nylon 6, Glass Fiber/Bead Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 126F2K4 is a 10% glass fibers and 20% glass beads filled polyamide 6 injection-molding-grade.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 5.90 GPa | 856 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.70 GPa | 682 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 38.0 kJ/m² @Temperature -30.0 °C |
18.1 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 43.0 kJ/m² @Temperature 23.0 °C |
20.5 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 4.40 J/cm² @Temperature -30.0 °C |
20.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 5.80 J/cm² @Temperature 23.0 °C |
27.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 184 °C | 363 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 213 °C | 415 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8311 (833-1) (UF) Synthetic Oil
- PTS Trilac® ABS-GF3000-BK 30% Fiberglass Black ABS Resin
- BP Amoco Amoco® 7942 Polypropylene Homopolymer (discontinued **)
- Saint-Gobain Norton® T-100 Virgin Skived PTFE Sheet (0.031" thick)
- A. Schulman PP 3369-01 Polypropylene Medium-Flow Homopolymer Polypropylene
- China Tungsten YG6 Tungsten Carbide
- Chosun Refractories GPB-1 Special brick
- CLAL-MSX CUPROROR® TL1 1/4 hard, Copper Alloy
- Colorite Polymers 7777 Non-Phthalate 77 Series Vinyl Compound
- Special Metals INCONEL® 686 Nickel Superalloy (UNS N06686) Sheet 0.125 in (3.2 mm)
Copyright © lookpolymers.com All Rights Reserved