- Sax Polymers SAXALEN PPC344G25 Polypropylene Copolymer, 25% Glass Filled
Sax Polymers SAXALEN PPC344G25 Polypropylene Copolymer, 25% Glass Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler |
| Manufacturer | Sax Polymers |
| Trade Name | SAXALEN |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXALEN PPC344G25 Polypropylene Copolymer, 25% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXALEN PPC344G25 is a 25% glass filled Polypropylene - Copolymer intended for injection molding.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Melt Flow | 24 g/10 min @Load 2.16 kg, Temperature 230 °C |
24 g/10 min @Load 4.76 lb, Temperature 446 °F |
from MVR; ISO 1033 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 53.0 MPa | 7690 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 4.50 GPa | 653 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 84.0 MPa | 12200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.80 GPa | 551 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 11.0 kJ/m² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 34.0 kJ/m² @Temperature -30.0 °C |
16.2 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 35.0 kJ/m² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 4.20 J/cm² @Temperature 23.0 °C |
20.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 114 °C | 237 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 250 °C | 428 - 482 °F | |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S70B Silicone Rubber
- Polykemi AB POLYfill PPC K5025 Polypropylene Copolymer, Mineral Reinforced
- Plaskolite West Optix® CA-82 UVA UV-Absorbing Acrylic Resin
- Momentive Performance Materials Ultraglaze® 4000 Construction Sealant
- Teknor Apex APEX® 3302-85 Polyvinyl Chloride, Flexible
- Zircar Zirconia ZYF-50 Zirconia Felt Insulation
- 3M FP089 Clear Polypropylene Label Products
- 3M Scotchcal™ 50-64 Graphic Film
- DSM Stanyl® TW200F3 Nylon 46-15% Glass Reinforced (European Grade) (Cond)
Copyright © lookpolymers.com All Rights Reserved