Azoty Tarnow™ TARNOFORM 500 UV POM

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer	Azoty Tarnow™ (Zaklady Azotowe)
Trade Name	TARNOFORM
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Azoty Tarnow™ TARNOFORM 500 UV POM.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High flow injection molding grade based on Tarnoform 500 modified with carbon black giving best weathering stability.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.

Physical Properties	Metric	English	Comments
Density	1.41 g/cc	0.0509 lb/in³	ISO 1183
Linear Mold Shrinkage	0.029 cm/cm	0.029 in/in	60x60x4
Linear Mold Shrinkage, Transverse	0.031 cm/cm	0.031 in/in	ISO 294-4
Melt Flow	23 g/10 min @Load 2.16 kg, Temperature 190 °C	23 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	115	115	ISO 2039-2
Ball Indentation Hardness	142 MPa	20600 psi	358 N; ISO 2039-1
Tensile Strength, Yield	58.0 MPa	8410 psi	ISO 527
Elongation at Break	14 %	14 %	ISO 527
Flexural Strength	61.0 MPa	8850 psi	ISO 178
Izod Impact, Notched (ISO)	5.00 kJ/m²	2.38 ft-lb/in²	1A; ISO 180
Charpy Impact, Notched	0.550 J/cm²	2.62 ft-lb/in²	1eA; ISO 179

Thermal Properties	Metric	English	Comments
Specific Heat Capacity	1.48 J/g-°C	0.354 BTU/lb-°F
Melting Point	167 °C	333 °F	10°C/min.; ISO 3146
Maximum Service Temperature, Air	100 °C	212 °F
Deflection Temperature at 1.8 MPa (264 psi)	147 °C	297 °F	ISO 75
Vicat Softening Point	147 °C	297 °F	50 N; ISO 306
Flammability, UL94	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm	IEC 60093
Surface Resistance	1.00e+15 ohm	1.00e+15 ohm	IEC 60093
Dielectric Constant	3.9 @Frequency 1e+6 Hz	3.9 @Frequency 1e+6 Hz	IEC 60250
Dielectric Strength	25.0 kV/mm	635 kV/in	IEC 60243
Dissipation Factor	0.0085 @Frequency 1e+6 Hz	0.0085 @Frequency 1e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	IEC 112

Processing Properties	Metric	English	Comments
Processing Temperature	180 - 230 °C	356 - 446 °F	Barrel temperature
Mold Temperature	60.0 - 120 °C	140 - 248 °F