SABIC Innovative Plastics LNP LUBRICOMP YP003 POLYESTER ELASTOMER
| Category | Polymer , Thermoplastic , Polyester, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP YP003 POLYESTER ELASTOMER.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* YP003 is a compound based on Polyester Elastomer resin containing 15% PTFE/Silicone. Added features of this material include: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 |
| 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.370 % | 0.370 % | 50% RH, 24 hrs; ASTM D570 |
| 0.500 % | 0.500 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.021 cm/cm @Time 86400 sec |
0.021 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0213 cm/cm @Time 86400 sec |
0.0213 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm @Time 86400 sec |
0.020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0205 cm/cm @Time 86400 sec |
0.0205 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 13.0 MPa | 1890 psi | ASTM D638 |
| 14.0 MPa | 2030 psi | ISO 527 | |
| Elongation at Yield | 39.9 % | 39.9 % | ISO 527 |
| 53.5 % | 53.5 % | ASTM D638 | |
| Tensile Modulus | 0.200 GPa | 29.0 ksi | 50 mm/min; ASTM D638 |
| 0.240 GPa | 34.8 ksi | 1 mm/min; ISO 527 | |
| Flexural Modulus | 0.260 GPa | 37.7 ksi | ASTM D790 |
| 0.270 GPa | 39.2 ksi | ISO 178 | |
| Izod Impact, Notched | 2.40 J/cm | 4.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 27.0 kJ/m² | 12.8 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 27.0 J | 19.9 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 26.0 J | 19.2 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.47 | 0.47 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.45 | 0.45 | ASTM D3702 Modified |
| K (wear) Factor | 10.1 x 10-8 mm³/N-M | 5.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 111 µm/m-°C @Temperature -40.0 - 40.0 °C |
61.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 111 µm/m-°C @Temperature -40.0 - 40.0 °C |
61.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 184 µm/m-°C @Temperature -40.0 - 40.0 °C |
102 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 184 µm/m-°C @Temperature -40.0 - 40.0 °C |
102 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C @Thickness 3.20 mm |
117 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 78 FRT 5 PP, glass fibre, mod. of mech. properties
- ND Industries 612 Heptane-Acetone Anaerobic Primer
- Polymer Resources PC/ABS-GP1-[color]-LG General Purpose PC/ABS Alloy, Low Gloss Grade
- PolyOne Therma-Tech™ NJC-8500 Nylon 12 (discontinued **)
- Polyram PlusTek PA4802G6BK10 Nylon 66 for Injection Molding, 30% Glass Fiber Reinforced, PTFE Lubricated
- Dow SPECFLEX™ NC 632 Polyol
- Covestro Makrolon® ET3127 Polycarbonate
- Arkema Group Rilsan® BZM 23 G9 Nylon 11, 23% Glass Fiber Filled (Dry)
- A. Schulman ComAlloy Hiloy® 627 Nylon 6/6, Mineral Reinforced
- A. Schulman POLYBATCH™ White LL8425 MG Concentrate Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved