- Samsung Cheil Industries Starex® TF-0930 MABS, Unreinforced Scratch Resistant
Samsung Cheil Industries Starex® TF-0930 MABS, Unreinforced Scratch Resistant
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® TF-0930 MABS, Unreinforced Scratch Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0040 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 3.20 mm |
0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 25 g/10 min @Load 10.0 kg, Temperature 220 °C |
25 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 60.8 MPa | 8820 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 12 % | 12 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.55 GPa | 370 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 93.2 MPa | 13500 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.84 GPa | 412 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.196 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.367 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
ASTM D256 |
| 0.196 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
0.367 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 | |
| 2.94 J/cm @Thickness 6.35 mm, Temperature -30.0 °C |
5.51 ft-lb/in @Thickness 0.250 in, Temperature -22.0 °F |
ASTM D256 | |
| 2.94 J/cm @Thickness 3.17 mm, Temperature -30.0 °C |
5.51 ft-lb/in @Thickness 0.125 in, Temperature -22.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 6.40 mm |
183 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 94.0 °C | 201 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm |
HB @Thickness 0.0591 - 0.118 in |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Pencil Hardness | 2H | 500g, JIS K 5401 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufTech™ GA-5062R PVC Compound
- ND Industries 533 Retaining Compound
- H.C. Starck Amperit® 553.074 Tungsten Carbide-Cobalt-Chromium 86-10-4 (WC-Co-Cr)
- Techmer ES HiFill® PA6 0177 B Barium Sulfate Filler
- SABIC Innovative Plastics LNP Verton RV008ESV PA 66
- SABIC Innovative Plastics NORYL PPX ZX09022 PPE+PP (Europe-Africa-Middle East)
- Master Bond EP21TDCF-3 Two Component, Higher Viscosity Epoxy System
- Zircar Refractory Composites RS-A3 Refractory Sheet
- Hexcel® HexForce™ SGP196-P Carbon Fabric
- ExxonMobil Exxtral™ LNU 011 Performance Polyolefin
Copyright © lookpolymers.com All Rights Reserved