Eastman Eastalloy DA003 PC+PCTG Copolyester/Polycarbonate (discontinued **)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polyester, TP , Polycyclohexylenedimethylene Terephthalate (PCT) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eastman Eastalloy DA003 PC+PCTG Copolyester/Polycarbonate
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ISO data as provided by the manufacturer, Eastman Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 5.5 % | 5.5 % | |
| Tensile Modulus | 1.97 GPa | 286 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | |
| 0.770 J/cm² @Temperature -30.0 °C |
3.66 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.0 µm/m-°C @Temperature 20.0 °C |
37.8 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature 20.0 °C |
27.8 µin/in-°F @Temperature 68.0 °F |
|
| Specific Heat Capacity | 1.38 J/g-°C | 0.330 BTU/lb-°F | |
| Melting Point | 249 °C | 480 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | |
| Vicat Softening Point | 110 °C | 230 °F | |
| Glass Transition Temp, Tg | 113 °C | 235 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
||
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Strength | 17.3 kV/mm | 439 kV/in | |
| Dissipation Factor | 0.0080 @Frequency 1e+6 Hz |
0.0080 @Frequency 1e+6 Hz |
|
| Comparative Tracking Index | 600 V | 600 V |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F |
Users viewing this material also viewed the following:
- H.C. Starck Amperit® 703.053 Chromium Oxide (Cr2O3) 99.5%
- Karina E 856-10/101-Y-ERYB White PVC Compound
- Solvay Specialty Polymers Meforex® 123 Ozone-Friendly CFC Replacement
- Sylvin Technologies 504 PVC Wire/Cable Compound
- A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6
- Eurotec® Tecotek® PC43 GR003 TD70 PC, unfilled, flame retardant - halogen (RoHS compliant), impact modified, light grey
- Arkema Group Rilsan® AMN G8 TLD Nylon 12, Graphite Filled (Dry)
- ExxonMobil 512 Mobilgard 12 Series
Copyright © lookpolymers.com All Rights Reserved