- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- Samsung Cheil Industries Starex® SR-0320 K ABS, Unreinforced Heat Resistant
Samsung Cheil Industries Starex® SR-0320 K ABS, Unreinforced Heat Resistant
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SR-0320 K ABS, Unreinforced Heat Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Water Absorption | 0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 3.20 mm |
0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 9.4 g/10 min @Load 10.0 kg, Temperature 220 °C |
9.4 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 113 | 113 | ASTM D785 |
| Tensile Strength, Yield | 41.2 MPa | 5970 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 35 % | 35 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.16 GPa | 313 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.86 J/cm @Thickness 6.35 mm |
3.49 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C @Thickness 6.40 mm |
201 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 106 °C | 223 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- MV Labs PT485 [Pt(NH3)4][PtCl4] Tetramineplatinum(II) tetrachloroplatinate(II)
- Resinlab® CYNERGY CA6011 Adhesive
- KEP Kepital® TX-31 Wear/Friction/Resistant Acetal Copolymer
- Michelman® Michem® Emulsion 91240G Nonionic polyethylene emulsion
- Lubrizol Advanced Materials Pearlbond® D170 Thermoplastic Polyurethane
- Ensinger TECAPEI® 10% Glass Reinforced, made from Ultem® 2100 PEI
- Eurostar Staramide RF007ESS PA66/6, 35% Glass Filled, Injection Molded
- ConocoPhillips Hydroclear® 68 Rolling Oil
- Lanxess Pocan® KU 2-7209 Z 901510 PBT, 15% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved