- Kuraray Genestarâ„¢ GC1201A-M41 Nylon, Glass Filled and Carbon Filled
Kuraray Genestarâ„¢ GC1201A-M41 Nylon, Glass Filled and Carbon Filled
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Kuraray Company |
| Trade Name | Genestar™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kuraray Genestarâ„¢ GC1201A-M41 Nylon, Glass Filled and Carbon Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Reinforced injection grade for conductive applications.Main Features:ConductivityHeat resistanceChemical resistanceExample of applications:Quick connector
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | |
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Water Absorption | 0.19 % | 0.19 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 170 MPa | 24700 psi | ISO 527-1/-2 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| Tensile Modulus | 10.9 GPa | 1580 ksi | ISO 527-1/-2 |
| Flexural Strength | 260 MPa | 37700 psi | ISO 178 |
| Flexural Modulus | 9.40 GPa | 1360 ksi | ISO 178 |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.0 µm/m-°C | 8.89 µin/in-°F | ASTM D696 |
| CTE, linear, Transverse to Flow | 39.0 µm/m-°C | 21.7 µin/in-°F | ASTM D696 |
| Melting Point | 300 °C | 572 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | ISO 75-1/-2 |
| Glass Transition Temp, Tg | 125 °C | 257 °F | 10°C/min; ISO 11357-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release Agent | |
| Applications | Automotive | |
| General Purpose | ||
| Chemical Resistance | Acid Resistance | |
| Alkali Resistance | ||
| Environmental Stress Crack Resistance | ||
| General Chemical Resistance | ||
| Grease Resistance | ||
| Hydrolytically Stable | ||
| Oil Resistance | ||
| Solvent Resistance | ||
| Delivery Form | Black | |
| Other Features | Barrier Properties | |
| Creep Resistance | ||
| High Crystalinity | ||
| Thermal Stability | ||
| Weldable | ||
| Regional Availability | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America | ||
| Special Characteristics | Heat Stabilized or Stable to Heat | |
| High Impact or Impact Modified |
Users viewing this material also viewed the following:
- ExxonMobil LD 135.09 Cast Packaging Film Resin (discontinued **)
- Ravago Manufacturing Americas Hylon® N1033L Nylon 6/6 (DAM) (discontinued **)
- Hong Kun Group AO 168 Antioxidant
- Lubriplate 930-AA Bentone Type Multi-Purpose Grease
- SABIC Innovative Plastics NORYL APS430 PPE+PPS (Asia Pacific)
- ExxonMobil LD 516.LN Molding, Extrusion and Compounding Resin
- Arlon 55579R033 0.033" (0.838 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- BASF Ultramid® 8202 L Intermediate PA6 (Conditioned)
- 3M FP012605 White Polyester Label Products
- Wanhua Chemical Wanthane® WHT-2195 Polycaprolactone Based TPU
Copyright © lookpolymers.com All Rights Reserved