- Polymer Property : Flexural Strength = 63.7 MPa
Polymer Property : Flexural Strength = 63.7 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D790 |
|
Samsung Cheil Industries Starex® SF-0505HWR MABS, Unreinforced Scratch Resistant
Information provided by Samsung Cheil Industries.
|
|||
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D790 |
|
Samsung Cheil Industries Starex® SF-0950S MABS, Unreinforced Scratch Resistant
Information provided by Samsung Cheil Industries.
|
|||
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D790 |
|
Samsung Cheil Industries Starex® SR-0305 ABS, Unreinforced Heat Resistant
Information provided by Samsung Cheil Industries.
|
|||
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D790 |
|
Samsung Cheil Industries Starex® SR-0320 K ABS, Unreinforced Heat Resistant
Information provided by Samsung Cheil Industries.
|
|||
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D638 |
|
Samsung Cheil Industries Starex® TX-0510 TRABS, Unreinforced
Information provided by Samsung Cheil Industries.
|
|||
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D638 |
|
Samsung Cheil Industries Starex® TX-0510T TRABS, Unreinforced
Information provided by Samsung Cheil Industries.
|
|||
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D638 |
|
Samsung Cheil Industries Starex® VE-0860 ABS, Unreinforced FR
Flame-retardant ABS with high heat resistance that can be used in battery cases and adaptorsInformation provided by Samsung Cheil Industries.
|
|||
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D638 |
|
Samsung Cheil Industries Starex® WR-9370 ASA, Unreinforced Heat Resistant
Information provided by Samsung Cheil Industries.
|
|||
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D790 |
|
Samsung Cheil Industries Starex® SF-0505HWR MABS, Unreinforced Scratch Resistant
Information provided by Samsung Cheil Industries.
|
|||
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D790 |
|
Samsung Cheil Industries Starex® SF-0950S MABS, Unreinforced Scratch Resistant
Information provided by Samsung Cheil Industries.
|
|||
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D790 |
|
Samsung Cheil Industries Starex® SR-0320 K ABS, Unreinforced Heat Resistant
Information provided by Samsung Cheil Industries.
|
|||
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D638 |
|
Samsung Cheil Industries Starex® TX-0510 TRABS, Unreinforced
Information provided by Samsung Cheil Industries.
|
|||
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D638 |
|
Samsung Cheil Industries Starex® TX-0510T TRABS, Unreinforced
Information provided by Samsung Cheil Industries.
|
|||
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D638 |
|
Samsung Cheil Industries Starex® VE-0860 ABS, Unreinforced FR
Flame-retardant ABS with high heat resistance that can be used in battery cases and adaptorsInformation provided by Samsung Cheil Industries.
|
|||
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D638 |
|
Samsung Cheil Industries Starex® WR-9120 J ASA, Unreinforced
Information provided by Samsung Cheil Industries.
|
|||
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D638 |
|
Samsung Cheil Industries Starex® WR-9370 ASA, Unreinforced Heat Resistant
Information provided by Samsung Cheil Industries.
|
|||
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D638 |
|
Samsung Cheil Industries Starex® WR-9120 J ASA, Unreinforced
Information provided by Samsung Cheil Industries.
|
|||
| Flexural Strength | 63.7 MPa | 9240 psi | 2.8 mm/min; ASTM D790 |
|
Samsung Cheil Industries Starex® SR-0305 ABS, Unreinforced Heat Resistant
Information provided by Samsung Cheil Industries.
|
|||
| Flexural Strength |
63.7
MPa <br>@Temperature 260 °C
|
9240
psi <br>@Temperature 500 °F
|
ASTM D790 |
|
Daelim H&L Plavis-G15 ISO 15% Graphite Filled Aromatic Polyimide Bearing
Isostatically Molded. Plavis-G-15: Graphite 15 wt% filled, Self lubricating grade for wear and friction applications.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded ..
|
|||
| Flexural Strength | 63.7 MPa | 9240 psi | ASTM D790 |
|
Daelim H&L Plavis-G40 DF 40% Graphite Filled Aromatic Polyimide Bearing
Direct Formed. Plavis-G-40: Graphite 40 wt% filled, Self lubricating grade with low thermal expansion.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded to 3 carbons is..
|
|||
Copyright © lookpolymers.com All Rights Reserved