Lehmann & Voss LUVOCOM® 1-1120 Polyamide 66, with PTFE, lubricant modified, high viscosity
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1-1120 Polyamide 66, with PTFE, lubricant modified, high viscosity.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteristics.Bearings, sleeves, sliding elements, control disks, gear wheels, duty parts in switches.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.015 - 0.025 cm/cm | 0.015 - 0.025 in/in | |
| Melt Flow | 10 g/10 min @Load 5.00 kg, Temperature 275 °C |
10 g/10 min @Load 11.0 lb, Temperature 527 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 75.0 MPa | 10900 psi | |
| Elongation at Yield | 5.0 % | 5.0 % | |
| 6.0 % | 6.0 % | flexural | |
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Flexural Strength | 110 MPa | 16000 psi | |
| Flexural Modulus | 2.50 GPa | 363 ksi | |
| Charpy Impact Unnotched | 12.0 J/cm² | 57.1 ft-lb/in² | flatwise; ISO 179 1fU |
| 7.00 J/cm² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Coefficient of Friction, Dynamic | 0.090 | 0.090 | |
| Coefficient of Friction, Static | 0.070 | 0.070 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 µm/m-°C | 33.3 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | |
| 160 °C | 320 °F | short term | |
| Vicat Softening Point | 230 °C | 446 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 290 °C | 554 °F | mass temp |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | |
| Zone 1 | 290 - 310 °C | 554 - 590 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 57600 sec |
167 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | dark grey |
Users viewing this material also viewed the following:
- PolyOne LubriOne™ AT-000/15T Acetal (POM) Copolymer
- ExxonMobil Escorene® LD-760 High EVA Compounding Resin (discontinued **)
- ExxonMobil Escorene® UL-7720 EVA Copolymer, Adhesive and Sealant Grade (discontinued **)
- MRC Polymers EMAREXâ„¢ 400 GF33 Nylon 6/6, 33% Glass Fiber Filled
- Total PS CPDS 801 Flame Retardant Polystyrene
- A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene
- CLAL-MSX NICLAFOR® 1000 TD1 Quenched/Cold Rolled, Rolled Copper Alloy
- Asahi Kasei Thermylene® P-10FG-2100 10% Glass Fiber Reinforced
- Nyco ULTRAFIBRE® 30 Wollastonite
- BP Amoco Acctuf® 3434 Impact Copolymer Polypropylene (discontinued **)