Lehmann & Voss LUVOCOM® 3/CF/10/BK Polyamide 6, with carbon fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 3/CF/10/BK Polyamide 6, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, apparatus- and precision engineering.High-strength and stiff parts; low coefficient of expansion.dynamic stressElectrically conductive, suitable for continuous discharging of statically generated electricity.Handles, levers, rollers, extrusion profiles.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ISO 1183 |
| Water Absorption | <= 1.3 % | <= 1.3 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 165 MPa | 23900 psi | |
| Elongation at Yield | 2.5 % | 2.5 % | |
| 3.2 % | 3.2 % | flexural | |
| Modulus of Elasticity | 8.50 GPa | 1230 ksi | |
| Flexural Strength | 240 MPa | 34800 psi | |
| Flexural Modulus | 7.00 GPa | 1020 ksi | |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
| 130 °C | 266 °F | short term | |
| Vicat Softening Point | 220 °C | 428 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1e+05 | <= 1e+05 | |
| Insulation Resistance | <= 100000 ohm | <= 100000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 °C | 518 °F | mass temp |
| Nozzle Temperature | 270 - 280 °C | 518 - 536 °F | |
| Zone 1 | 250 - 270 °C | 482 - 518 °F | |
| Zone 2 | 270 - 290 °C | 518 - 554 °F | |
| Zone 3 | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Drying Temperature | 75.0 °C @Time 36000 - 57600 sec |
167 °F @Time 10.0 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Nye Lubricants 761G Grease
- Mytex Polymers AX1162 Polypropylene, Glass filled, Compounded
- Kinlead LSS11 Low Temperature Grade Heat Sealable Film (thickness: 30 µm)
- LATI Latene® AG7H2 G/50 PP Homopolymer, 50% Glass Fiber Reinforced, Heat Stabilized
- LATI Latigray 82-03 CW/95 PA 12, Metallic Reinforced
- A. Schulman POLYBATCH™ Green 30394 Concentrate Based In LDPE
- Denka VINYKON TS1007T PVC, S grade for window frame gaskets
- Diamond Polymers ABS 3500 Natural 1003 Injection Molding Grade, High Flow, Medium Impact, Low Gloss
- Akzo Nobel Trigonox® BPIC-C75 Polymerization Initiator
- SABIC Innovative Plastics LNP Thermocomp PF007 PA 6 (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved