A. Schulman ComAlloy Hiloy® 221 ABS, Glass Reinforced, UL
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Hiloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Hiloy® 221 ABS, Glass Reinforced, UL.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.10% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 97.0 MPa | 14100 psi | ASTM D790 |
| Flexural Modulus | 3.90 GPa | 566 ksi | ASTM D790 |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.46 J/cm | 4.61 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 235 - 266 °C | 455 - 511 °F |
Users viewing this material also viewed the following:
- RheTech Products T15P100-00 12% Talc Reinforced Polypropylene, Natural
- Pau Tai UNISTAB ECZ-84A Stabilizers for Cable
- Dielectric Polymers NT-988-2 Overlap Splice Tape (discontinued **)
- LG Chemical LUCON CP-4201F Conductive Thermoplastic, Flame Retardant
- LATI Latamid 66 H2 G/35-V0KB PA 66, 35% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 350ºF Cure Temperature
- ChevronTexaco Rando® HD 100
- Dow VORANOL™ CP 6001 Polyol
- Aclo Accutech Polypropylene Homopolymer HP0334T40L Talc Reinforced
- Wanhua Chemical Wanthane® WHT-1564 Polyester Based TPU
Copyright © lookpolymers.com All Rights Reserved