SABIC Innovative Plastics LNP LUBRICOMP KCL36 Acetal Copoly (Asia Pacific)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP KCL36 Acetal Copoly (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* KCL36 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.
Physical Properties Metric English Comments
Density 1.58 g/cc
0.0571 lb/in³
ASTM D792
1.58 g/cc
0.0571 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0069 cm/cm

@Time 86400 sec
 0.0069 in/in

@Time 24.0 hour
 ISO 294
0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.010 - 0.012 cm/cm

@Time 86400 sec
 0.010 - 0.012 in/in

@Time 24.0 hour
 ASTM D955
0.011 cm/cm

@Time 86400 sec
 0.011 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 117 MPa
17000 psi
ASTM D638
117 MPa
17000 psi
ISO 527
Tensile Strength, Yield 117 MPa
17000 psi
ASTM D638
117 MPa
17000 psi
ISO 527
Elongation at Break 1.4 %
1.4 %
ASTM D638
1.4 %
1.4 %
ISO 527
Elongation at Yield 1.4 %
1.4 %
ASTM D638
1.4 %
1.4 %
ISO 527
Tensile Modulus 17.32 GPa
2512 ksi
1 mm/min; ISO 527
20.68 GPa
2999 ksi
50 mm/min; ASTM D638
Flexural Strength 179 MPa
26000 psi
ASTM D790
179 MPa
26000 psi
ISO 178
Flexural Modulus 16.54 GPa
2399 ksi
ASTM D790
17.3 GPa
2510 ksi
ISO 178
Izod Impact, Notched 0.480 J/cm
0.899 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.80 J/cm
8.99 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 27.0 kJ/m²
12.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 9.00 J
6.64 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.38
0.38
ASTM D3702 Modified
Coefficient of Friction, Static 0.31
0.31
ASTM D3702 Modified
K (wear) Factor 127 x 10-8 mm³/N-M
63.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 43.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 23.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
43.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 24.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 27.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 15.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
27.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 15.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 163 °C
325 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
162 °C

@Thickness 3.20 mm
 324 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 159 °C
318 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
160 °C

@Thickness 3.20 mm
 320 °F

@Thickness 0.126 in
 unannealed; ASTM D648