- HOME
- POLYMER SEARCH
- Thermoplastic
- Polycarbonate (PC)
- Polycarbonate/ABS Alloy, Unreinforced
- Samsung Cheil Industries Infino® WP-1098 PC/ABS, Unreinforced
Samsung Cheil Industries Infino® WP-1098 PC/ABS, Unreinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® WP-1098 PC/ABS, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 3.20 mm |
0.0050 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 3.20 mm |
0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 30 g/10 min @Load 10.0 kg, Temperature 250 °C |
30 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 111 | 111 | ASTM D785 |
| Tensile Strength at Break | 48.8 MPa | 7080 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.67 GPa | 242 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 70.6 MPa | 10200 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 2.01 GPa | 292 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 1.47 J/cm @Thickness 6.35 mm, Temperature -30.0 °C |
2.76 ft-lb/in @Thickness 0.250 in, Temperature -22.0 °F |
ASTM D256 |
| 1.57 J/cm @Thickness 3.17 mm, Temperature -30.0 °C |
2.94 ft-lb/in @Thickness 0.125 in, Temperature -22.0 °F |
ASTM D256 | |
| 3.43 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
6.43 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
ASTM D256 | |
| 6.08 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
11.4 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C @Thickness 6.40 mm |
239 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C @Thickness 6.40 mm |
223 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 120 °C | 248 °F | B/50; ISO R306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 35 % @Temperature 23.0 °C |
35 % @Temperature 73.4 °F |
50% RH, 60°; ASTM D2457 |
Users viewing this material also viewed the following:
- PolyOne Bergamid™ A70 white Polyamide 66 (Nylon 66)
- Renegade Materials Corporation RM-5001 Cyanate Ester Prepreg, 6781 S2 Glass Fabric
- LG Chemical LUPOL GP3202 PP+MF20%
- Kotec Carbotex K-30UV Polycarbonate, General Purpose, UV Stability Grade
- Haynes 556® alloy, bar, after 8000 hours at 650°C (1200°F)
- Wellman Wellamid® GF13-66 22LH-NBK1 13% Glass Fiber Reinforced, General Purpose Nylon 66
- A. Schulman POLYFORT™ PP 2175HU-31 High Flow Copolymer Polypropylene
- Akzo Nobel Trigonox® SBP-W50 Polymerization Initiator
- Applied Composites 8049 Polyester SMC
Copyright © lookpolymers.com All Rights Reserved