EMS-Grivory Grivory® TSM-30/4 PA666-MD30
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, Mineral Reinforced |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® TSM-30/4 PA666-MD30.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Water Absorption | 6.0 % | 6.0 % | ISO 62 |
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm | 0.014 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 135 MPa | 19600 psi | conditioned; ISO 2039-1 |
| 180 MPa | 26100 psi | dry; ISO 2039-1 | |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | conditioned; ISO 527-1/-2 |
| 85.0 MPa | 12300 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 7.0 % | 7.0 % | dry; ISO 527-1/-2 |
| 35 % | 35 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 2.10 GPa | 305 ksi | conditioned; ISO 527-1/-2 |
| 4.80 GPa | 696 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature 30.0 °C |
19.0 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU |
| 5.00 J/cm² @Temperature 30.0 °C |
23.8 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | dry; ISO 179/1eA |
| 0.500 J/cm² | 2.38 ft-lb/in² | conditioned; ISO 179/1eA | |
| 0.300 J/cm² @Temperature 30.0 °C |
1.43 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 0.400 J/cm² @Temperature 30.0 °C |
1.90 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 90.0 - 120 °C | 194 - 248 °F | long term; EMS |
| 180 °C | 356 °F | short term; EMS | |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | conditioned; IEC 60093 |
| 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Granules | |
| Processing | Injection Molding |
Users viewing this material also viewed the following:
- Nyco NYGLOS® 4W STO105 Wollastonite in Polypropylene
- Meilian Chemical PE2306 BLACK MASTERBATCH
- Lucent Polymers PBT-FR310 Polybutylene Terephthalate, Flame Resistant
- Zeon Chemicals Zeonex® E48R Cyclo-Olefin Polymer
- Arlon Thermabond® R36300W008 0.008" (0.203 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
- 3M Scotch Pad™ 8327 Custom Carry Handle
- 3M Scotchkote™ 80EG 531 Urethane Elastomer
- Hexion Bakelite™ EP 8412 Epoxy Resin, High Arc Resistance, Improved Electrical Properties, Low Shrinkage
Copyright © lookpolymers.com All Rights Reserved