Samsung Cheil Industries Infino® GW-3130 PC, 10% Glass Filled Recycled
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® GW-3130 PC, 10% Glass Filled Recycled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Eco-friendly Post-Consumer recycled content.Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Water Absorption | 0.050 % @Temperature 23.0 °C |
0.050 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0040 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0050 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 9.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
9.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| 17 g/10 min @Load 10.0 kg, Temperature 250 °C |
17 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 | |
| Ash | 10 % | 10 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength at Break | 35.3 MPa | 5120 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 13 % | 13 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.24 GPa | 469 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 88.3 MPa | 12800 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 3.14 GPa | 455 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.77 J/cm @Thickness 6.35 mm |
3.31 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 2.45 J/cm @Thickness 3.17 mm |
4.59 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 6.40 mm |
288 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 145 °C | 293 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 0.800 - 3.20 mm |
HB @Thickness 0.0315 - 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.8 | 2.8 | STM D150 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® C4960 TPE, Transparent
- Fujipoly Industries Sarcon® 45T Thin-Film TR
- Iran Petrochemical (PCC) 12XF6 Linear Low Density Polyethylene
- SABIC Innovative Plastics Ultem AUT230M PEI (Asia Pacific)
- Styron XZ 94462.01 Carboxylated SB
- Master Bond EP40 High Shear and Peel Strength, Two Component, Flexible Epoxy
- EDRO P1FM #31 Free Machining Holder Steel
- Eurofoam Siliconcell 412/BT 130 Silicone Foam
- PolyOne Lubri-Tech™ MP-30GF/15T Modified PPO - 30% Glass Fiber - 15% PTFE (discontinued **)
- DuPont Performance Polymers Hypalon® 40S Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound (disco
Copyright © lookpolymers.com All Rights Reserved