SABIC Innovative Plastics Xylex X8419 PC+POLYESTER

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polyester, TP
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Xylex
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Xylex X8419 PC+POLYESTER.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Low-medium flow, suitable for blow molding, injection molding, extrusion.This data was supplied by SABIC-IP for the Americas region.

Physical Properties	Metric	English	Comments
Specific Gravity	1.20 g/cc	1.20 g/cc	ASTM D 792
Density	1.20 g/cc	0.0434 lb/inÂ³	ISO 1183
Moisture Absorption at Equilibrium	0.050 %	0.050 %	23Â°C / 50% RH; ISO 62
Water Absorption at Saturation	0.12 % @Temperature 23.0 Â°C	0.12 % @Temperature 73.4 Â°F	ISO 62
Linear Mold Shrinkage, Flow	0.0050 - 0.0080 cm/cm @Thickness 3.20 mm	0.0050 - 0.0080 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	6.0 g/10 min @Load 2.16 kg, Temperature 265 Â°C	6.0 g/10 min @Load 4.76 lb, Temperature 509 Â°F	ASTM D 1238
	6.0 g/10 min @Load 2.16 kg, Temperature 265 Â°C	6.0 g/10 min @Load 4.76 lb, Temperature 509 Â°F	[cm^3/10 min] Melt Volume Rate; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	55.0 MPa	7980 psi	Type I, 50 mm/min; ASTM D 638
	110 MPa	16000 psi	50 mm/min; ISO 527
Tensile Strength, Yield	55.0 MPa	7980 psi	Type I, 50 mm/min; ASTM D 638
	60.0 MPa	8700 psi	50 mm/min; ISO 527
Elongation at Break	120 %	120 %	50 mm/min; ISO 527
	130 %	130 %	Type I, 50 mm/min; ASTM D 638
Elongation at Yield	5.8 %	5.8 %	50 mm/min; ISO 527
	6.0 %	6.0 %	Type I, 50 mm/min; ASTM D 638
Tensile Modulus	1.90 GPa	276 ksi	1 mm/min; ISO 527
	2.10 GPa	305 ksi	5 mm/min; ASTM D 638
Flexural Yield Strength	80.0 MPa	11600 psi	2 mm/min; ISO 178
	85.0 MPa	12300 psi	1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus	2.00 GPa	290 ksi	1.3 mm/min, 50 mm span; ASTM D 790
	2.05 GPa	297 ksi	2 mm/min; ISO 178
Izod Impact, Notched	0.700 J/cm @Temperature -30.0 Â°C	1.31 ft-lb/in @Temperature -22.0 Â°F	ASTM D 256
	7.50 J/cm @Temperature 23.0 Â°C	14.1 ft-lb/in @Temperature 73.4 Â°F	ASTM D 256
Izod Impact, Notched (ISO)	7.00 kJ/mÂ² @Temperature -30.0 Â°C	3.33 ft-lb/inÂ² @Temperature -22.0 Â°F	80104; ISO 180/1A
	11.0 kJ/mÂ² @Temperature 23.0 Â°C	5.23 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1A
Charpy Impact, Notched	1.80 J/cmÂ² @Temperature 23.0 Â°C	8.57 ft-lb/inÂ² @Temperature 73.4 Â°F	V-notch Edgew 80104 sp=62mm; ISO 179/1eA
Impact Test	68.0 J @Temperature 23.0 Â°C	50.2 ft-lb @Temperature 73.4 Â°F	Instrumented Impact Total Energy; ASTM D 3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	69.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	38.3 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
	71.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	39.4 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
CTE, linear, Transverse to Flow	69.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	38.3 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
	71.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	39.4 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi)	98.0 Â°C	208 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	98.0 Â°C @Thickness 3.20 mm	208 Â°F @Thickness 0.126 in	unannealed; ASTM D 648
Vicat Softening Point	115 Â°C	239 Â°F	Rate B/50; ASTM D 1525
	115 Â°C	239 Â°F	Rate B/50; ISO 306
	115 Â°C	239 Â°F	Rate B/120; ISO 306

Optical Properties	Metric	English	Comments
Haze	<= 2.0 % @Thickness 2.54 mm	<= 2.0 % @Thickness 0.100 in	ASTM D 1003
Transmission, Visible	89 % @Thickness 2.54 mm	89 % @Thickness 0.100 in	ASTM D 1003

Users viewing this material also viewed the following: