Hexcel® F161 Epoxy Resin, 285 Kevlar Fabric

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® F161 Epoxy Resin, 285 Kevlar Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hexcel designation: 285-38"-F161; Fiber: Kev. 49 1140Information provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 253 MPa

@Temperature 177 °C
 36700 psi

@Temperature 351 °F
 Wet
259 MPa

@Temperature 132 °C
 37600 psi

@Temperature 270 °F
 Wet
281 MPa

@Temperature 177 °C
 40800 psi

@Temperature 351 °F
 Dry
349 MPa

@Temperature 132 °C
 50600 psi

@Temperature 270 °F
 Dry
392 MPa

@Temperature -54.0 °C
 56900 psi

@Temperature -65.2 °F
 Dry
399 MPa

@Temperature 24.0 °C
 57900 psi

@Temperature 75.2 °F
 Wet
428 MPa

@Temperature 24.0 °C
 62100 psi

@Temperature 75.2 °F
 Dry
Tensile Modulus 20.2 GPa

@Temperature 177 °C
 2930 ksi

@Temperature 351 °F
 Wet
21.8 GPa

@Temperature 177 °C
 3160 ksi

@Temperature 351 °F
 Dry
24.5 GPa

@Temperature 132 °C
 3550 ksi

@Temperature 270 °F
 Wet
24.7 GPa

@Temperature 132 °C
 3580 ksi

@Temperature 270 °F
 Dry
25.1 GPa

@Temperature 24.0 °C
 3640 ksi

@Temperature 75.2 °F
 Wet
25.2 GPa

@Temperature -54.0 °C
 3660 ksi

@Temperature -65.2 °F
 Dry
26.5 GPa

@Temperature 24.0 °C
 3840 ksi

@Temperature 75.2 °F
 Dry
Compressive Yield Strength 52.0 MPa

@Temperature 177 °C
 7540 psi

@Temperature 351 °F
 Wet
71.0 MPa

@Temperature 132 °C
 10300 psi

@Temperature 270 °F
 Wet
85.0 MPa

@Temperature 177 °C
 12300 psi

@Temperature 351 °F
 Dry
104 MPa

@Temperature 132 °C
 15100 psi

@Temperature 270 °F
 Dry
128 MPa

@Temperature 24.0 °C
 18600 psi

@Temperature 75.2 °F
 Wet
199 MPa

@Temperature -54.0 °C
 28900 psi

@Temperature -65.2 °F
 Dry
308 MPa

@Temperature 24.0 °C
 44700 psi

@Temperature 75.2 °F
 Dry
Compressive Modulus 12.1 GPa

@Temperature 177 °C
 1750 ksi

@Temperature 351 °F
 Wet
15.2 GPa

@Temperature 132 °C
 2200 ksi

@Temperature 270 °F
 Wet
15.6 GPa

@Temperature 177 °C
 2260 ksi

@Temperature 351 °F
 Dry
17.2 GPa

@Temperature 132 °C
 2490 ksi

@Temperature 270 °F
 Dry
19.7 GPa

@Temperature 24.0 °C
 2860 ksi

@Temperature 75.2 °F
 Wet
24.8 GPa

@Temperature -54.0 °C
 3600 ksi

@Temperature -65.2 °F
 Dry
28.1 GPa

@Temperature 24.0 °C
 4080 ksi

@Temperature 75.2 °F
 Dry
Shear Strength 11.0 MPa

@Temperature 177 °C
 1600 psi

@Temperature 351 °F
 Short Beam
14.0 MPa

@Temperature 177 °C
 2030 psi

@Temperature 351 °F
 Short Beam
17.0 MPa

@Temperature 132 °C
 2470 psi

@Temperature 270 °F
 Short Beam
23.0 MPa

@Temperature 132 °C
 3340 psi

@Temperature 270 °F
 Short Beam
29.0 MPa

@Temperature -54.0 °C
 4210 psi

@Temperature -65.2 °F
 Short Beam
30.0 MPa

@Temperature 24.0 °C
 4350 psi

@Temperature 75.2 °F
 Short Beam
30.0 MPa

@Temperature 24.0 °C
 4350 psi

@Temperature 75.2 °F
 Short Beam
Descriptive Properties Value Comments
Cured Thickness per Ply (cm) 0.025
Laminate
Dry Resin Content (%) 47-53
Prepreg
Fiber Volume (%) 47.9
Laminate
Flow (%) 20-30