- Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
- Samsung Cheil Industries Starex® WR-9120AT ASA, Unreinforced
Samsung Cheil Industries Starex® WR-9120AT ASA, Unreinforced
| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® WR-9120AT ASA, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Used in washing machine cover etc.Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Melt Flow | 15 g/10 min @Load 10.0 kg, Temperature 220 °C |
15 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Yield | 48.1 MPa | 6970 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 60 % | 60 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 65.7 MPa | 9530 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 2.16 GPa | 313 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 1.18 J/cm @Thickness 3.17 mm |
2.20 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C @Thickness 6.40 mm |
180 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 97.0 °C | 207 °F | B/50; ISO R306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistivity per Square | 1.10e+11 ohm @Temperature 23.0 °C |
1.10e+11 ohm @Temperature 73.4 °F |
50% RH; ASTM D250 |
| Static Decay | 3.0 sec @Temperature 23.0 °C |
3.0 sec @Temperature 73.4 °F |
50% RH; JIS L1049 |
Users viewing this material also viewed the following:
- Polymer Resources PPX-MF-FR3 Modified-PPO, V-0 Flame Retardant, Mineral Reinforced
- Humiseal 1B73 Acrylic Conformal Coating
- MarkeTech Calcium Carbonate, Calcite (CaCO3) Optical Grade Crystal
- Greene Tweed CHEMRAZ® 513 Perfluoroelastomer
- Stir SpA AF 91 (PVC)
- Eastman Eastar DN004HF Copolyester
- Abatron Epotron 5 Clear Liquid Epoxy Adhesive for Structural Bonding
- 3M 8420-6 Cold Shrink Connector Insulators
- Advanced Elastomer Systems Santoprene® 101-64 W175 Thermoplastic Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved